The effects of ultrasonic-aided quenching (USQ) on the microstructure and corrosion properties of 35CrMoV steel in a simulated seawater environment (wt % (NaCl) = 3.5) were studied. The corrosion properties of the steel were studied by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. The scanning electron microscope (SEM) and energy dispersive spectrometer (...

In order to control the corrosion in pipelines, it is important to understand the underlying corrosion mechanisms and predict ion of it’s initiation and means of mitigation. This paper reviews the electrochemistry of corrosion, it’s kinetics and thermodynamic nature, with respect to CO2 and H2S effects in propagating corrosion in oil and gas pipeline system. The phenomenon of polarization and i...

The electrochemical corrosion behavior of a silver-plated circuit board (PCB-ImAg) in a polluted marine atmosphere environment (Qingdao in China) is studied through a simulated experiment. The morphologies of PCB-ImAg show some micropores on the surface that act as the corrosion-active points in the tests. Cl- mainly induces microporous corrosion, whereas SO₂ causes general corrosion. Notably, ...

The corrosion behavior of three sorts of refractories based on alumina-graphite were studied by immersion tests. The melts included smelting reduction molten slag and corresponding carbon saturated molten iron. The influence of test temperature, FeO content in slag and specimen rotative velocity on the corrosion rate of refractories was examined. By means of SEM and EDS, the microstructure chan...

The corrosion fatigue performance of high-strength bolt was studied. Based on the fracture mechanics theory and the Gerberich-Chen formula, the high-strength bolt corrosion fracture crack model and the fatigue life model were established. The high-strength bolt crack depth and the fatigue life under corrosion environment were quantitatively analyzed. The factors affecting high-strength bolt cor...

Erosion, corrosion, and erosion-corrosion are common problems in offshore pipelines, tubing and pipe fittings. Corrosion has an important impact on the total cost of oil and gas production. Considering the diversity of corrosion related problems, CO2 corrosion (sweet corrosion) is probably the material degradation mechanism most extensively assessed in this industry over the last 30 years. In t...

The crevice correction is a common type of localized corrosion which costs multibillion dollar losses in many different fields including aerospace, automobile, and building structures. The crevice geometry can easily catch moisture and impurity which accelerates the chemical corrosion. It is one of the dangerous corrosions that can cause sudden failure of the products and involve the human inju...

This Module consists of ten Web pages of required reading. The pagination is visible at the bottom of each page with direct links to adjacent pages. Introduction Thermodynamic principles can help explain a corrosion situation in terms of the stability of chemical species and reactions associated with corrosion processes. However, these principles cannot be used to predict corrosion currents or ...

The aim of this article is to review those aspects of corrosion behaviour that are most relevant to the clinical application of implant alloys. The special modes of corrosion encountered by implant alloys are presented. The resistance of the different materials against the most typical corrosion modes (pitting corrosion, crevice corrosion and fretting corrosion) is compared, together with obser...

Atmospheric corrosion is a significant problem given destruction of various materials, especially metals. The corrosion investigation in the industrial city environment was carried out during one year exposure. Corrosion potential was determined using the potentiometric method. The highest effect of corrosion processes was observed during the winter season due to increased air pollution. Corros...