STATEMENT OF PROBLEM Bonded porcelain veneers are widely used esthetic restorations. Although high success and survival rates have been reported, failures occur. Fracture is the most common failure mode. Fractures range from incomplete cracks to the catastrophic. Minimally invasive or thin partial veneers have gained popularity. PURPOSE The aim of this study was to measure the influences of p...

PURPOSE The color of the ceramic restorations is affected by various factors such as brand, thickness of the layered the ceramic, condensation techniques, smoothness of surface, number of firings, firing temperature and thickness of dentin. The aim of this study was to evaluate the color change and surface roughness in dental porcelain with different thicknesses during repeated firings. MATER...

STATEMENT OF PROBLEM Bonded porcelain veneers are widely used esthetic restorations. High success and survival rates have been reported, but failures do occur. Fractures are the commonest failure mode. Minimally invasive or thin veneers have gained popularity. Increased enamel and porcelain thickness improve the strength of veneers bonded to enamel, but less is known about dentin or mixed subst...

Introduction: The purpose of the presented study was to evaluate the effect of zirconia thickness on the tensile stress of zirconia based all-ceramic restorations. Methods: Twenty zirconia disks with 10mm diameter were prepared in two groups using CAD/CAM system. The thickness of zirconia was 0.5mm in first group and 0.3mm in second group. After sintering, 0.4mm glass ceramic porcelain was appl...

Porcelain laminate veneers are used routinely in cosmetic dentistry. The public usually refers to this mode of treatment simply as “veneers.” Their popularity has increased because of television makeover programs, commercials, and magazine advertisements. Porcelain laminate veneers have so increased in their attractiveness that the general public is demanding this type of instant makeover. Furt...

This paper deals with the influence of selected methods (mechanical and pneumatic) as well as various factors (wood species, moisture content, veneer shape, punch diameter, laminating foil thickness, holding method, plasticizing) on 3D molding of veneers. 3D molding was evaluated on the basis of maximum deflection of birch and beech veneers. Cracks and warping edges were also evaluated in selec...

The aim of this study was to determine the effect of different ceramic thickness on heat generation during resin cement photo-activation by QTH (quartz-tungsten-halogen), LED (light emitting diode), and PAC (plasma arc-curing) LCUs (light curing units). The resin cement used was Rely X ARC (3M-ESPE), and the ceramic was IPS Empress Esthetic (Ivoclar-Vivadent), of which 0.7-, 1.4- and 2.0-mm thi...

PURPOSE In this prospective clinical study, the performance of three- and four-unit fixed partial dentures (FPDs) with frameworks fabricated of yttria partially stabilized zirconia was determined after a mean observation period of 50 months. The study focused on the survival of the restoration (in situ criterion) and the success of the ceramic veneers (no defect). MATERIALS AND METHODS Sevent...

STATEMENT OF PROBLEM Zirconia-based restorations have the common technical complication of delamination, or porcelain chipping, from the zirconia core. Thus the shear bond strength between the zirconia core and the veneering porcelain requires investigation in order to facilitate the material's clinical use. PURPOSE The purpose of this study was to evaluate the bonding strength of the porcela...

OBJECTIVE The purpose of this study was to determine whether the bond of veneering porcelain to a ceramic core in bilayered ceramics was similar to that of the metal ceramic control of well known behaviour. STUDY DESIGN Six groups of nine specimens each were fabricated, whose dimensions were 15 mm long and 8 mm in diameter at the core, and 2 mm long and 8 mm in diameter for the veneer. The gr...