Context: Nanocomposites are becoming popular today because of the manufacturers claiming high surface smoothness and good abrasion resistance properties thus improving the longevity of the restoration. Aims: This in vitro study was carried out to investigate the effect of nanofillers on surface roughness and abrasion resistance of nanofilled compositeFiltek Z350 (3M ESPE) and nanohybrid composi...

AIM The aim of this study was to evaluate the clinical performance of direct resin composite restorations (Tetric Ceram-TC) and indirect composite inlays (Targis-TG) after 12 months. METHODS AND MATERIALS Seventy-six Class I and II restorations (44 direct and 32 indirect) were inserted in premolars and molars with carious lesions or deficient restorations in 30 healthy patients according to t...

PURPOSE The aim of this study was to evaluate the biaxial flexural strength (BFS) of one zirconia-based ceramic used with various veneering ceramics. MATERIALS AND METHODS Zirconia core material (Katana) and five veneering ceramics (Cerabien ZR; CZR, Lava Ceram; LV, Cercon Ceram Kiss; CC, IPS e.max Ceram; EM and VITA VM9; VT) were selected. Using the powder/liquid layering technique, bilayere...

THE PURPOSE of the study was to analyse translucency parameter (TP values) of glass-ceramics fabricated by different techniques and investigate the effect of the corrosive medium on TP values. MATERIALS AND METHODS Three specimens of each type of IPS e.max ceramics (Ivoclar Vivadent, Schaan, Liechtenstein) were made in three colours (A2, C2 and B3) by three fabrication techniques (layering - ...

This study evaluated: (1) the effect of different ceramics on light attenuation that could affect microhardness, measured as the Knoop Hardness Number (KHN), of a resin cement immediately and 24 hours after polymerization and (2) the effect of different activation modes (direct light-activation, light activation through ceramics and chemical activation) on the KHN of a resin cement. Resin cemen...

Simultaneous application of colloidal processing and liquidforming additives to alumina resulted in a sintered density of >99% in 1 h at a temperature as low as 1070°C for a commercial high-purity alumina powder at a total dopant level of 2 mol%. The additives were 0.9% CuO + 0.9% TiOz + 0.1% B 2 0 3 + 0.1% MgO. At higher temperatures or after prolonged sintering, the doped alumina ceramic deve...

A comparison has been made of the infrared spectra of alumina with molybdenum oxide alumina in both the oxidized and reduced forms. In the case of molybdena-alumina prepared via adsorption of gaseous MoOp(OH)t, the spectra show that a practically complete monolayer of Mo6+ oxide covers the alumina. After reduction with hydrogen the hydroxyls of the carrier appear. From the reversibility of redu...

Improving the bond strength of veneering ceramics to ZrO2-based cores remains a challenge. The purpose this study was evaluate shear different ZrO2 containing calcium silicate (CaSi) ceramics. Five types (n = 230) were divided into two groups: with or without oxygen plasma treatment. These bound (IPS e.max Ceram VITA VM9). Shear various measured 10), in addition phase composition, surface morph...

Porous alumina film on aluminum with gel-like pore wall was prepared by a two-step anodization of aluminum, and the corresponding gel-like porous film was etched in diluted NaOH solution to produce alumina nanowires in the form of densely packed alignment. The resultant alumina nanowires were reacted with NH(3) and evaporated aluminum at an elevated temperature to be converted into densely pack...

The growth of ordered nanorods of mesoporous SBA-15 inside a porous alumina membrane has been achieved for the first time by a simple sol-gel method. The obtained SBA-15 nanorods themselves have ordered hexagonal mesochannels with a size of about 6 nm and have been arranged to form hexagonal arrays by the limitation of pores of the alumina membrane. The synthesized alumina membrane with mesopor...