The nature and distribution of residual stresses are invariably critical for fatigue life with dissimilar material joints often inducing high tensile residual stresses. A fatigue-resistant concept of weld cladding process pipelines, producing compressive residual stresses, is under investigation to examine how these stresses may be influenced. Simplified weld cladding simulations have successfu...

This paper discusses the modeling of residual stresses in fracture problems. Historically, residual stress effects in fracture have focused on the crack driving force, so that solely opening mode residual stresses are assumed to influence fracture. However, residual stresses can effect all components of stress at the crack-tip, and can thereby alter crack-tip constraint and influence material t...

Two-dimensional finite element modeling procedures are addressed to predict the residual stresses for multipass welds. A generalized plane strain model with a five-pass weld in a plate and an axisymmetric model with a six-pass girth weld in a pipe are considered. Element rebirth and pass-lumping techniques are employed in both models. The combined heat input using surface and body flux componen...

Tube hydroforming (THF) process is used to produce the complex components from the initial cylindrical tubes. In this paper, T- shape component was formed using a tube hydroforming machine and the residual stresses of hydroformed tube was determined by hole drilling method. Subsequently, the thickness distribution and residual stresses of final tube were investigated using experimental and fini...

after springs production, different residual stresses are created in the inner and outer surfaces of spring wires. some of these stresses for example compressive residual stresses are useful and some are harmful. the effects of vareation of these stresses are caused spring relaxation and decrising in their free length when they are loaded intermittently. for review this phenomena in this resear...

In this paper, we estimate the stresses and strains from the equatorial region down to the apex of the heart by modeling the passive left ventricle as a frustrum of a thick hollow cone. Large deformation theory has been employed in this analysis. Furthermore, the eeects of residual stresses and the anisotropy due to muscle ber orientation have been included. It is observed that circumferential ...

To improve the manufacturing quality of welded structures, to prevent failures at weld joints and to predict their lifetime, measurements of the residual stresses generated by welding in the structures are extremely useful. The residual stresses may reduce the component life due to phenomena that occur at low applied stresses such as brittle fracture, fatigue and stress corrosion cracking. Weld...

We report on the residual stresses in amorphous shape memory polymers reinforced with SiC particles. After 50% compression of the composite material at 25 °C, the SiC particles exhibit a compressive stress, which is almost completely released during heated recovery at 120 °C. The residual stresses in SiC hexagonal (6H) phase were estimated through the average change of the unit-cell volume. Lat...

Many of the degradation mechanisms relevant to power plant components can be exacerbated by stresses that reside within the material. Good design or structural integrity assessments require therefore, an accounting of residual stresses, which often are introduced during welding. To do this it is necessary to characterise the stresses, but this may not be possible in thick components using non-d...

In this study, the tensile strength, impact strength, and the hardness of the weld are determined. A criterion is proposed for describing the effect of residual stress on the weld mechanical properties. Dimensionless parameters such as Rya (the average of residual stress over the material yield strength), Rym (the maximum residual stress over the material yield strength), ...