The purpose of this study is to understand the electrochemical corrosion behavior of 1wt% Cu content Al-6Si-0.5Mg alloy in 0.1M NaCl solution. The potentiodynamic polarization curves reveal that 1wt% Cu content alloy is less prone to corrosion than the Cu free alloy. The EIS test results show that corrosion resistance or polarization resistance (Rct) increases with the addition of 1wt% Cu to Al...

Pitting corrosion due to microbial activity is the most severe type of corrosion that occurs in ship hull. Since biogenic sulfide produced by sulfate-reducing bacteria (SRB) is involved in the acceleration of pitting corrosion of marine vessels, so it is important to collect information about SRB community involved in maritime vessel failure. We investigated the SRB community on corroded hull p...

Cu60Zr30Ti10 metallic glass powder was prepared by mechanically alloying a mixture of pure Cu, Zr, and Ti powders after 5 h of milling. Cu60Zr30Ti10 bulk metallic glass (BMG) was synthesized by vacuum hot pressing the as-milled Cu60Zr30Ti10 metallic glass powder at 746 K in the pressure range of 0.72–1.20 GPa, and the structure was analyzed through X-ray diffraction and transmission electron mi...

stress-corrosion cracking (scc) tests were conducted in the near-neutral ph standard solution, ns4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...

Abstract This work investigated the electrochemical and aqueous tribological behavior of hot pressed 2205 duplex stainless steel (DSS). DSS sintered composites of different volume percent (% vol) of partially stabilized zirconia (PSZ) was developed using powder metallurgy (PM) technique. Electrochemical behaviour was studied at room temperature, using open circuit potential and potentiody...

This paper describes the non-uniform corrosion characteristics and mechanical properties of reinforcement under coupled action of carbonation and static loading. The two parameters, namely area-box (AB) value and arithmetical mean deviation (Ra), are adopted to characterize the corrosion morphology and pitting distribution from experimental observations. The results show that the static loading...

The corrosion behaviour of three new non-toxic titanium alloys for use as biomaterials has been investigated. The corrosion current densities of these Ti alloys have low values, indicating a passive state that is stable with time. These values were calculated by using both direct and alternate current methods. The comparison with Ti–6Al–4V, widely used as biomaterial, shows slightly lower corro...

Corrosion is one of the degrading mechanisms that greatly affect the structural integrity of aerospace components. Corrosion begins with small imperfections in the given material referred to as “pits”. Over time, and with exposure to the environment and loading stresses, these pits grow into structural cracks. These cracks, under further exposure to elements and stress, will eventually lead to ...

The electrochemical corrosion behavior of NiTi alloy electrodeposited conductive polypyrrole (PPy) coatings doped with small size sulfate (SO42 ), medium size para-toluene sulfonate (pTS ) and large size dodecylbenzene sulfonate (DBS ) counter anions has been studied by electrochemical measurements and surface analysis. It is demonstrated that PPy coatings inhibit the corrosion of NiTi substrat...

steel corrosion of bars in concrete structures is a complex process which leads to the reduction of the cross-section bars and decreasing the resistance of the concrete and steel materials. in this study, reliability analysis of a reinforced concrete beam with corrosion defects under the distributed load was investigated using the enhanced hasofer-lind and rackwitz-fiessler (ehl-rf) method base...