Ultra High Cycle fatigue leads to a failure initiated in the bulk material of a material. Some results on the nodular cast iron are presented: initiation occurs from the defects, located at the surface or in the bulk. It has been shown that environment plays a major role that could explain the difference between fatigue lives, for the surface and internal initiation. The influence of the defect...

Combined high and low cycle fatigue (CCF) generally induces the failure of aircraft gas turbine attachments. Based on the aero-engine load spectrum, accurate assessment of fatigue damage due to the interaction of high cycle fatigue (HCF) resulting from high frequency vibrations and low cycle fatigue (LCF) from ground-air-ground engine cycles is of critical importance for ensuring structural int...

Jet Propulsion Laboratory California Institute of Technology Pasadena, CA 91109 Differential expansion induced fatigue resulting from temperature cycling is a leading cause of solder joint failures in spacecraft. Achieving high reliability flight hardware requires that each element of the fatigue issue be addressed carefully. This includes defining the complete thermal-cycle environment to be e...

AIM To evaluate the bending fatigue lifetime of nickel-titanium alloy (NiTi) and stainless steel (SS) endodontic files using finite element analysis. METHODOLOGY The strain-life approach was adopted and two theoretical geometry profiles, the triangular (TR) and the square cross-sections, were considered. Both low-cycle fatigue (LCF) lifetime and high-cycle fatigue (HCF) lifetime were evaluate...

S. Bulatović, Yugoslav River Shipping, Serbia, Z. Burzić, Military Technical Institute, Serbia, V. Aleksić, Institute for Testing Materials, Serbia, A. Sedmak, University of Belgrade, Faculty of Mechanical Engineering, Serbia, Lj. Milović, University of Belgrade, Faculty of Technology and Metallurgy, Serbia High strength low-alloy steel under low cycle fatigue at a certain level of strain contr...

A multiscale fatigue analysis model is developed for brittle composite materials. The mathematical homogenization theory is generalized to account for multiscale damage effects in heterogeneous media and a closed form expression relating nonlocal microphase fields to the overall strains and damage is derived. The evolution of fatigue damage is approximated by the first order initial value probl...