The effect of recasting, up to two times, Ni-Cr (DUCINOX) prosthetic alloy on its corrosion properties was carried out. The corrosion measurements were done in deoxygenated Fusayama Meyer artificial saliva solution at temperature of 37°C. In the study following electrochemical methods were used: measurement of free corrosion potential Ecor in open circuit, measurement of polarization resistance...

Under badly environmental conditions as well as complex loads, corrosion of embedded reinforcing steel bars in concrete is common for reinforced concrete (RC) structures. Fatigue of corrosion reinforcing steel bars is a key problem for old RC bridges. To assess the residual fatigue life of aged existing RC bridges, the most new study information on fatigue of natural corrosion reinforcement is ...

The corrosion resistance of a Magnesium alloy is low and needs to be improved. This research aimed at corrosion-resistance improvement by supatterd deposition aluminium film, which is formed on the surface of AZ91 Magnesium-alloy. Corrosion resistance performed polarization curve measurement, was evaluated in quest of the corrosion rate using the Tafel extrapolation method, and conducted surfac...

The effects of ultrasonic-aided quenching (USQ) on the microstructure and corrosion properties of 35CrMoV steel in a simulated seawater environment (wt % (NaCl) = 3.5) were studied. The corrosion properties of the steel were studied by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. The scanning electron microscope (SEM) and energy dispersive spectrometer (...

In order to control the corrosion in pipelines, it is important to understand the underlying corrosion mechanisms and predict ion of it’s initiation and means of mitigation. This paper reviews the electrochemistry of corrosion, it’s kinetics and thermodynamic nature, with respect to CO2 and H2S effects in propagating corrosion in oil and gas pipeline system. The phenomenon of polarization and i...

The electrochemical corrosion behavior of a silver-plated circuit board (PCB-ImAg) in a polluted marine atmosphere environment (Qingdao in China) is studied through a simulated experiment. The morphologies of PCB-ImAg show some micropores on the surface that act as the corrosion-active points in the tests. Cl- mainly induces microporous corrosion, whereas SO₂ causes general corrosion. Notably, ...

The corrosion behavior of three sorts of refractories based on alumina-graphite were studied by immersion tests. The melts included smelting reduction molten slag and corresponding carbon saturated molten iron. The influence of test temperature, FeO content in slag and specimen rotative velocity on the corrosion rate of refractories was examined. By means of SEM and EDS, the microstructure chan...

The corrosion fatigue performance of high-strength bolt was studied. Based on the fracture mechanics theory and the Gerberich-Chen formula, the high-strength bolt corrosion fracture crack model and the fatigue life model were established. The high-strength bolt crack depth and the fatigue life under corrosion environment were quantitatively analyzed. The factors affecting high-strength bolt cor...

Erosion, corrosion, and erosion-corrosion are common problems in offshore pipelines, tubing and pipe fittings. Corrosion has an important impact on the total cost of oil and gas production. Considering the diversity of corrosion related problems, CO2 corrosion (sweet corrosion) is probably the material degradation mechanism most extensively assessed in this industry over the last 30 years. In t...

The crevice correction is a common type of localized corrosion which costs multibillion dollar losses in many different fields including aerospace, automobile, and building structures. The crevice geometry can easily catch moisture and impurity which accelerates the chemical corrosion. It is one of the dangerous corrosions that can cause sudden failure of the products and involve the human inju...