A new mixed-mode threshold stress intensity factor is developed using a critical plane-based multiaxial fatigue theory and the Kitagawa diagram. The proposed method is a nominal approach since the fatigue damage is evaluated using remote stresses acting on a cracked component rather than stresses near the crack tip. An equivalent stress intensity factor defined on the critical plane is proposed...

This paper proposes a reliable and cost-effective two-phase methodology to predict crack propagation life in generic two-dimensional (2D) structural components. First, the usually curved fatigue crack path and its stress-intensity factors are calculated at small crack increments in a specialized finite-element software, using automatic remeshing algorithms, special crack tip elements and approp...

This paper evaluates the effects of microbiologically influenced corrosion (MIC) on fatigue-crack growth of candidate materials useful in expanding bio-ethanol usage, including a storage-tank steel (ASTM A36) and two pipeline steels (API 5L X52 and X70). The microbiological species sampled and cultivated from an ethanol fuel production stream are responsible for both acetic acid and hydrogen su...

Compressive failure by splitting is studied herein via an analytical model. The use of a shear lag model to determine the stress state at the crack tip and the modeling of the region away from the crack tip by the 3D elasticity equations leads to a simple analytical expression is used to determine the compliance changes for both unsteady crack growth as well as steady state crack growth under c...

Fatigue of materials, like alloys, is basically fatigue-crack growth in small cracks nucleating and growing from micro-structural features, such as inclusions voids, or at micro-machining marks, large to failure. Thus, the traditional nucleation stage (Ni) microcracks (initial flaw sizes 1 30 μm about 250 μm) metal alloys. crack-growth tests were conducted on a 9310 steel under laboratory air r...

Modeling of stress corrosion cracking (SCC) is performed using the combination of the finite element method and the symmetric Galerkin boundary element method. The uncracked structural component is represented with finite elements. The crack is simulated using the boundary element method. The superposition principle is employed for combining two solutions. The equilibrium state for the system o...

Fatigue properties and cracking behavior of cold-drawn commercially pure aluminum wires (CPAWs) widely used as the overhead transmission conductors were investigated. It was found that the fracture surface of the CPAWs shows an obvious four-stage fracture characteristic, i.e., crack initiation, planar crack propagation, 45°-inclined crack propagation and final rapid fracture. The crack growth m...

The SGBEM-FEM alternating method suitable for the solution of elastic and elasticplastic three-dimensional fracture mechanics problems is presented. The crack is modeled by the symmetric Galerkin boundary element method (SGBEM), as a distribution of displacement discontinuities in an infinite medium. The finite element method (FEM) is used for stress analysis of the uncracked finite body. The s...