محمد ذاکری
پژوهشکده سرامیک، پژوهشگاه مواد و انرژی، کرج
[ 1 ] - سنتز و سینتر درجای اسپینل شفاف آلومینات منیزیم نانوساختار با روش سینتر جرقه پلاسمای واکنشی
در این پژوهش سرامیک شفاف اسپینل آلومینات منیزیم نانوساختار بدون هیچ‌گونه کمک سینتر با استفاده از مواد اولیه نانوسایز آلومینا و منیزیای دارای خلوص متفاوت به روش سینتر جرقه پلاسمای واکنشی در دمای °C 1250 به مدت min 10 سنتز و سینتر درجا شد. تراکم، ریزساختار و خواص اپتیکی نمونه‌های تهیه شده مورد بررسی قرار گرفت. نتایج نشان داد که با افزایش خلوص مواد اولیه، میزان عبور اپتیکی افزایش یافته و میزان آن ...
[ 2 ] - In-situ Fabrication of Transparent Magnesium Aluminate Spinel by Spark Plasma Sintering
Transparent polycrystalline spinel ceramic was fabricated without any sintering aids by spark plasma sintering method of a mixture of Al2O3 and MgO powders for only 10min soak at 1250°C. Densification, microstructure and optical transparency of spinel were examined. The spinel exhibits an in-line transmission of 55% for a visible-wavelength of 470nm and high hardness value of 2040 HV.
[ 3 ] - Investigation of Effective Parameters on Densification of ZrB2-SiC Based Composites Using Taguchi Method
Abstract The main goal of this study is optimization of densification of ZrB2-SiC composites reinforced with chopped Cf prepared by SPS. Taguchi method is employed as statistical design of experiment (DOE) to optimize densification parameters including SiC, Cf, MoSi2, HfB2 and ZrC content, milling time of Cf and SPS parameters such as temperature, time and pressure. Each of these factors ...
[ 4 ] - Electrical Resistivity Measurement of the Molten Cordierite Glass Using Two-wire method
Electrical resistivity (ER) is a main parameter in the melting processes of glasses. However, its measurement is difficult at high temperatures. In this study the electrical resistivity of different cordierite glass samples in the molten state was measured in the temperature range of 1100˚C to 1550 ˚C using the two-wire method. It was attempted to decrease the electrical resistivity of the glas...
[ 5 ] - Effect of Chromium Content on Formation of (Mo1-x-Crx) Si2 Nanocomposite Powders via Mechanical Alloying
(Mo1-x-Crx)Si2 composite powders were successfully synthesized by ball milling of Mo, Cr and Si elemental powders. Effects of the Cr content, milling time and annealing temperature were investigated. X-ray diffraction (XRD) was used to characterize the milled and annealed powders. The morphological and microstructural evolutions were studied by scanning electron microscopy (SEM) and transmissio...
[ 6 ] - Crystal Structure and Lattice Parameter Investigation of La3+ Substituted CeO2 in LaxCe1-xO2-X/2 Synthesized by Solid-State Method
Lanthanum (La) doped Ceria (CeO2) has attracted considerable interest as a candidate material for thermal barrier coating (TBC) because of its low thermal conductivity and potential capability to be operated above 1250°C. In this study, La2Ce2O7 powder was synthesized through the ball mill method. The crystal structure of La3+ su...
[ 7 ] - سینتر نانوکامپوزیت ZrB2-SiC-ZrC با استفاده از جرقۀ پلاسما (SPS) از پودرهای سنتز شده به روش MASPS
در این پژوهش از پودر نانوکامپوزیتی ZrB2-SiC-ZrC سنتز شده به روش MA-SPS که روش سنتز جدیدی برای این کامپوزیت محسوب می‌شود، جهت سینتر کامپوزیت ZrB2-SiC-ZrC به روش SPS استفاده شد. در این پژوهش سازکار سینترشدن یه وسیلۀ نمودارهای مستخرج از فرایند SPS شامل نمودار جایجایی-دما-زمان، سرعت جابجایی – دما و سرعت جابجایی – زمان بررسی شد. فرایند سینتر شدن کامپوزیت در دمای C°1750 و زمان min 17 کامل شد. با استف...
نویسندگان همکار