[ 1 ] - Effect of nitriding temperature on the nanostructure and corrosion properties of Nickel coated 304 stainless steel
Nickel films of 150 nm thickness were deposited on 304 stainless steel and post annealed under flow of nitrogen at different temperatures. The prepared samples were corrosion tested in 1.0 M H2SO4 solution using potentiodynamic polarization technique. Crystallographic and morphological structure of the samples were analysed by X-ray diffraction XRD and atomic force microscopy AFM respectively b...
[ 2 ] - Influence of nitrogen ion implantation on the nanostructure and corrosivity of Ni/stainless steel substrates
Ion implantation is a surface modification technology to produce new material on the surface by impingement of high energy ions from the ion accelerator. In this work, AISI 304 stainless steels were coated with 90 nm Ni film by electron beam deposition and implanted by a flow of 5×1017 N cm−2 at 400 K temperature with different implantation energies of 10, 20, 30 and 40 keV. The prepared sample...
نویسندگان همکار