N. Barati

2Department of Materials Science and Engineering, Sharif University of Technology, Azadi Street, P.O. Box 11365-9466, Tehran, Iran

[ 1 ] - Alumina nanostructured coating for corrosion protection of 316L stainless steel

Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...

[ 2 ] - Alumina nanostructured coating for corrosion protection of 316L stainless steel

Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...

نویسندگان همکار