School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.
[ 1 ] - STUDY ON NIOBIUM CARBIDE COATING FORMATION ON AISI L2 STEEL USING THERMO-REACTIVE DEPOSITION METHOD
In the present research, to form niobium carbide coating on the surface of AISI L2 steel Thermo-Reactive Deposition method (TRD) in a molten bath was used. Niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4, and 8 hours. The molten bath contained 20wt.% borax (Na2B4O7), 5 wt.% boric acid (B2O3), and 75 wt.% ferro-niobium. The presence and properties of...
[ 2 ] - Kinetic Study of Niobium Carbide Coating Formation on AISI L2 Steel using Thermo-Reactive Deposition Technique
In the present study, Thermo-Reactive Deposition method (TRD) in a molten bath was used to form niobium carbide coating on AISI L2 steel. The coating was formed in five different composition of borax (Na2B4O7), boric acid (B2O3), and ferro-niobium. For all of the five compositions of molten bath, niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4 and 8 hour...
نویسندگان همکار