[ 1 ] - Microwave-Hydrothermal Synthesis and Characterization of High-Purity Nb Doped BaTiO3 Nanocrystals
The synthesis of Nb doped BaTiO3 has been investigated under Microwave-Hydrothermal (MH) conditions in the temperature of 150°C for only 2 h using C16H36O4Ti, BaH2O2.8H2O and NbCl5 as Ba, Ti and Nb sources, respectively. Typical experiments performed on MH processing have not yet reported for Nb doped BaTi...
[ 2 ] - Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave
Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...
[ 3 ] - Convectional hydrothermal synthesis of high-purity pesudo-cubic BaTi0.09Nb0.01O3 nanocrystals in rotary autoclave
Nano-sized BaTiO3 powders with particular Nb concentrations were prepared by Rotary- Hydrothermal (RH) method. Hydrothermal method was used at 180 °C for 5 hours with new Ti pressure and the teflon vessel was rotated at a speed of 160 rpm during the hydrothermal reaction. New hydrothermal method was used instead of previous solid state reaction for the system BaTiO3±Nb<sub...