[ 1 ] - Determination of solution temperature in an ex-service Ni-based turbine blade
It is well-known that the harsh operational conditions of turbine blades lead to a gradual change in the microstructure of underlying Ni-based superalloy of blades. According to this, a rejuvenation process should be conducted on turbine blades superalloys to recover their microstructures. The first and main step of rejuvenation process is the determination of appropriate solution condition in ...
[ 2 ] - Cyclic oxidation behavior of uncoated and aluminum-rich nickel aluminide coated Rene-80 superalloy
In this study, aluminide coating was employed to enhance the high-temperature cyclic oxidation of Rene-80 superalloy at 950ºC. The microstructural aspects and phase constituents of samples were investigated with scanning electron microscopy (SEM) and x-ray diffraction (XRD) techniques. The result of oxidation tests showed that the weight gain in the uncoated sample was considerably higher than...
[ 3 ] - Effect of NiTi Addition on the Wear Resistance of YSZ Coatings
In this study, small fraction of NiTi (5 wt%) was added to Yttria stabilized zirconia (YSZ) top coat to improve it sliding wear resistance. The measurement of width of wear tracks after wear tests under a 15 N load for 100 m sliding distances showed that the width of wear track in NiTi-YSZ coating is shorter than that in YSZ coating which depicts the higher wear resistance of NiTi-YSZ coa...