[ 1 ] - Fabrication of the Cu-Zn multilayer and Cu-Zn alloy by accumulative roll bonding (ARB) with an emphasis on the wear behavior
Accumulative roll bonding (ARB) was used to fabricate the Cu-Zn multilayer and Cu-Zn solid solution. A lamellar structure with the hardness of about 130 VHN was formed after eight ARB cycles. Following to the suitable heat treatment, a solid solution with a uniform microstructure and hardness of about 57 VHN was produced. The dominant wear mechanism in the ARB processed multilayer was found to ...
[ 2 ] - Formation of a solid solution through accumulative roll bonding (ARB) and post-heat treatment of multilayered Cu/Zn/Al
In the present study, the capability of accumulative roll bonding (ARB) and subsequent heat-treatment to fabricate solid solution from a multilayered Cu/Zn/Al was investigated. Two post-heat treatment (one-step and two-step) routes were proposed. In the first, the ARB processed material was heated to 800 C for 5:30 hours and allowed to cool slowly in a furnace (one-step route). In the second (t...
نویسندگان همکار