N. Anjabin
shiraz university
[ 1 ] - Modeling and Experimental Study of Static Recovery and Mechanical Behavior of AA5052 Alloy During Cold-Working and Subsequent Annealing
In the present study, the mechanical behavior of AA5052 aluminum alloy during cold deformation and subsequent isothermal annealing in a temperature range of 225-300oC was investigated using the uniaxial tensile test data. It is found that by increasing the annealing time and temperature the material yield strength is decreased. The microstructural investigations of the annealed samples show tha...
[ 2 ] - Hot Deformation Behavior of Ni80A Superalloy During Non-Isothermal Side Pressing
In the present study, the microstructural changes of a Nickel based superalloy Nimonic80A during a non-isothermal deformation were studied. Therefore, microstructure evolutionduring hot side pressing test was predicted with combined methods of finite element analysis andprocessing map of the material. The predicted results were validated through experimentalmicrostructural studies. The results ...
[ 3 ] - Modeling of Corrosion-Fatigue Crack Growth Rate Based on Least Square Support Vector Machine Technique
Understanding crack growth behavior in engineering components subjected to cyclic fatigue loadings is necessary for design and maintenance purpose. Fatigue crack growth (FCG) rate strongly depends on the applied loading characteristics in a nonlinear manner, and when the mechanical loadings combine with environmental attacks, this dependency will be more complicated. Since, the experimental inv...