[ 1 ] - The Influence of Hematite on High Speed Continuous Casting of Steel Lubricating Powders: Viscosity and Crystallization
Mold powders used in the continuous casting of steel contain the harmful CaF2 as a main substance developing toxic gases such as SiF4 and HF at elevated temperatures. In this study, three samples of I1, I2 and I3, which contained gypsum free Portland cement clinker with different percentages of Fe2O3 (5.68, 6.83, 8.02 ...
[ 2 ] - The Impact of MnO, Li2O, ZnO and TiO2 on Mold Powders Viscosity Using Hot Stage Microscope Analysis
The aim of conducting this research was to evaluate the viscosity change in the continuous casting of steel mold powders by altering their chemical compositions, using hot stage microscope analysis. 4 low-fluorine samples containing such compositions as MnO, Fe2O3, Li2O, TiO2 and ZnO, as well as another fluorine-free sample containing a combination of Fe2O3 and TiO2, were prepared in this resea...
[ 3 ] - Effects of Replacing Fluorine with Sodium and Titanium Oxides on Continuous Casting of Steel Mold Powders Lubrication
Mold powders are used as raw materials in continuous casting of steel industry; Also they are mostly composed of aluminum, calcium, silica oxides, alkaline and earth-alkaline oxides along with carbon and fluor. Two of the most important duties of mold powders are the lubrication of the space between mold walls and steel shell, and heat transfer control between steel shell and the copper mold. F...