The effect of TiO2 concentration on microstructure, corrosion behavior and wear behavior of Ni-P-W-TiO2 coating

نویسنده

  • ,
چکیده مقاله:

Nickel-phosphorus coatings (Ni-P) are widely used in industry due to their high hardness, corrosion resistance and very good mechanical and chemical properties. Oxide particles such as TiO2 can be used to increase the wear resistance of these coatings. In this study, the Ni-P-W-TiO2 composite coating was deposited on the AISI 304L steel substrate using the electroplating method. Electroplating was performed at concentrations of 10, 20, and 30 g/L TiO2, and the effect of TiO2 concentrations on the microstructure, corrosion behavior, and wear behavior was investigated. Coatings were characterized by scanning electron microscopy (SEM). In order to investigate corrosion resistance, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests were used in 3.5% NaCl aqueous solution. A pin on disk test was used to test the wear resistance of uncoated and coated samples. Sample micro-hardness was also measured by the Vickers hardness test. Examination of the microstructure showed that the best TiO2 concentration for deposition was 20 g/L. The results of Tafel and electrochemical impedance spectroscopy tests were also consistent with microscopic images, and the results showed that the coating formed at concentration of 20 g/L had the highest corrosion resistance compared to other coated and non-coated samples. Also, the results of the wear test showed that increasing the TiO2 concentration increases the micro-hardness and wear resistance.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of TiO2 Particle Concentration on Microstructure and Mechanical Properties of Ni-P-TiO2 Composite Coatings

Ferritic stainless steels are widely used in equipment, including parts in turbines, electrical industries, aerospace, automotive and decorating industries. One of the problems with this type of steels is their low wear resistance. One of the ways to overcome this problem is to apply a wear-resistant coating on the surface of steel. In this research, nickel phosphorus-titanium oxide coating was...

متن کامل

Effect of nano-Al2O3 particles concentration on microstructure and corrosion behavior of Co-P-nano-Al2O3 composite coating

Composite coatings containing P and ceramic particles are considered in terms of properties such as corrosion resistance, oxidation resistance and high hardness. In this study, Co-P-nanoAl2O3 composite coating was fabricated on the AISI 430 stainless steel substrate using a direct current electric deposition technique. The quality of the coating and its corrosion resistance were studied by chan...

متن کامل

Effect of current density on the microstructure and polarization resistance of Ni-P-TiO2-ZrO2 composite coating

Composite coatings with nickel matrix and ceramic reinforcement particles have high ability to improve surface properties, such as good corrosion and abrasion resistance. In this study, Ni-P composite coating was coated with ZrO2 and TiO2 ceramic particles on the AISI 316 steel substrate through direct current plating method. The effect of the current densities of 20, 30, 40 and 50 mA/cm2 on th...

متن کامل

Wear behavior of carbon steel electrodeposited by nanocrystalline Ni–W coating

Ni-W coatings, compared to pure nanocrystalline Ni, exhibit higher hardness and wear resistance. In some cases, these coatings are considered as environmental friendly alternatives for hard chromium coating. Till now, most of Ni-W coatings have been produced by direct current electrodeposition from alkaline baths. In this study square pulse current was used for deposition of Ni-W precipitates f...

متن کامل

Effect of Nano-TiO2 Particles on the Corrosion Behavior of Chromium-Based Coatings

Nanosized TiO2 particles were prepared by sol–gel method. The TiO2 particles were co-deposited with chromium using electrodeposition technique. In investigating of coating surfaces by scanning electron microscope (SEM), the results showed that the morphology of the coating surface was changed by adding TiO2 nanoparticles to the chromium coating. The corrosion behavior of the coatings was assess...

متن کامل

The effect of pH on the morphology and polarization resistance of Ni-P-TiO2-ZrO2 composite coating

Nickel field composite coatings have a high ability to improve surface properties, such as increased corrosion resistance and abrasion resistance. In this study, Ni-P-TiO2-ZrO2 composite coating on AISI 316L steel substrate was deposited by direct current flow method and the effects of different pH 3, 3.5, 4 and 4.5 on coating morphology and corrosion resistance were investigated. Scanning elec...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 10  شماره 1

صفحات  25- 43

تاریخ انتشار 2021-07

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

کلمات کلیدی برای این مقاله ارائه نشده است

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023