TAPE CASTING OF NON-AQUEOUS HYDROXYAPATITE SLIPS
نویسندگان
چکیده مقاله:
Thin sheets of hydroxyapatite were fabricated by tape casting process. The non-aqueoustape casting formulation was optimized by adjusting the concentration of organic additivesspecially those of binder and plasticizer in the slurry. The optimized slurry was cast on a glasscarrier using a designed laboratory scale doctor blade. Following a binder removal stage, thetapes were sintered at different temperatures in air atmosphere. Heat treatment at 1250 °C led tothe formation of a dense microstructure as was evidenced by the scanning electron microscopy.
منابع مشابه
Ceramic planar waveguide laser of non-aqueous tape casting fabricated YAG/Yb:YAG/YAG
Ceramic YAG/Yb:YAG/YAG planar waveguide lasers were realized on continuous-wave and mode-locked operations. The straight waveguide, fabricated by non-aqueous tape casting and solid state reactive sintering, enabled highly efficient diode-pumped waveguide continuous-wave laser with the slope efficiency of 66% and average output power of more than 3 W. The influence of the waveguide structure on ...
متن کاملPreparation of hexaferrite multilayers by tape casting
Tape casting technics were used to realize a screen with continuous change in characteristics. Different hexaferrite compositions owned by the Ba3C02-~Zn~Fe24041 (Z) family were synthetized by coprecipitation method and calcined at 1200 "C in air. Then a slurry containing this powder is slip casted using tape casting. The tapes are dried under magnetic fied in order to orient the magnetic plate...
متن کاملInvestigation of the mechanical properties of various yttria stabilized zirconia based thin films prepared by aqueous tape casting
In this study various yttria doped zirconia based thin films were prepared by the aqueous tape casting method. The rheological property of the paste was studies. The phase content and microstructure of the samples was investigated by X-ray diffraction and scanning electron microscope, respectively. The mechanical properties of thin films were studied by Vickers microhardness and nanoindentatio...
متن کاملUltrasonic deagglomeration of AI2O3 and BaTiO3 for tape casting
Ultrasonic agitation is a very efficient method for deagglomeration and dispersion of ceramic slurries (alumina and barium titanate). The influence of parameters such as acoustic power, temperature, and treatment duration on the dispersion efficiency has been studied. For
متن کاملFreeze casting of hydroxyapatite scaffolds for bone tissue engineering.
Although extensive efforts have been put into the development of porous scaffolds for bone regeneration, with encouraging results, all porous materials have a common limitation: the inherent lack of strength associated with porosity. Hence, the development of porous hydroxyapatite scaffolds has been hindered to non-load bearing applications. We report here how freeze casting can be applied to s...
متن کاملEthanol-based Tape Casting Process of the Textured Bi0.5(Na0.80K0.20)0.5TiO3-BiFeO3 Ceramics
The rheological and tape casting behavior of ethanol-based Bi0.5(Na0.80K0.20)0.5TiO3-7 mol% BiFeO3 (BNKT-BF) slurries was investigated. The effect of sintering temperature profile on texture development with a preferred orientation was also studied. A 50 MPa pressure assisted three step sintering profile promoted extensive texture development together with densification. The role of BF as a sin...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 1 شماره 4
صفحات 9- 15
تاریخ انتشار 2004-12
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023