Synthesis of Tantalum Carbide/Boride Nano Composite Powders by Mechanochemical Method
نویسندگان
چکیده مقاله:
In this study, mechanochemcical process(MCP) is applied to synthesize ultrafine TaC powders. In this research, nano powder composite TaC-TaB2 was produced using mixtures of tantalum carbide and boron carbide as raw materials via mechanochemical process. The phase formation characterization during process was utilized by X-ray diffractometry (XRD). The morphology of synthesized powder was studied using scanning electron microscopy (SEM).
منابع مشابه
SYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD
The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...
متن کاملThermal Plasma Synthesis of Nano-sized Powders
Thermal plasmas, normally generated by DC (direct current) arc or inductively coupled RF (Radio Frequency) discharge, can be described as a high enthalpy flame with extremely high temperature fields (1,000~20,000 K) and a wide range of velocity fields from several m/s [1-5] to supersonic values [6-7]. Since the resultant huge enthalpy can be realized for various kinds of plasma forming gases an...
متن کاملSurfactant Effect on the Synthesis of B4C-nano TiB Composite by Co-precipitation Method
Titanium diboride is one of the candidate materials for high temperature applications and also for control rod elements in high temperature reactors. This paper presents the experimental data on the composites of B4 C-nano TiB2 that were synthesized successfully by co-precipitation methodat 1523K. Titanium tetraisopropanol, boron carbide, isopropanol and triton x-100were used as the precursor m...
متن کاملbuckling of viscoelastic composite plates using the finite strip method
در سال های اخیر، تقاضای استفاده از تئوری خطی ویسکوالاستیسیته بیشتر شده است. با افزایش استفاده از کامپوزیت های پیشرفته در صنایع هوایی و همچنین استفاده روزافزون از مواد پلیمری، اهمیت روش های دقیق طراحی و تحلیل چنین ساختارهایی بیشتر شده است. این مواد جدید از خودشان رفتارهای مکانیکی ارائه می دهند که با تئوری های الاستیسیته و ویسکوزیته، نمی توان آن ها را توصیف کرد. این مواد، خواص ویسکوالاستیک دارند....
Synthesis of HfB2 Powders by Carbothermal Reduction
In this research, solid state carbothermal synthesis of HfB2 Nano powders was investigated. For this purpose, HfO2,H3BO3, carbon active or phenolic resin were used as raw materials for carbothermal reaction. After 2-4 hours of milling the raw materials by a planetary ball in an ethanol media, the mixture was heat dried and pressed in to disks under pressure of 20-30 bar. The disks were then pla...
متن کاملPREPARATION AND SINTERING OF W-20%Wt Cu COMPOSITE POWDERS PRODUCED BY CO-PRECIPITATION METHOD
Abstract: materials can be fabricated by sintering of W-Cu composite powders. In this research W-20%wt Cu composite powderswas synthesized via a co-precipitation method. Precipitate obtained from a mixture of copper nitrate and ammoniumparatungstate (APT) in distilled water contained W-Cu compounds. This precipitate was washed, dried and calcinedat 550 of dried precipitate powder was determined...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 27 شماره 5
صفحات 769- 774
تاریخ انتشار 2014-05-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023