Synthesis of mesoporous TiO2-SiO2-Ag and investigation of its structural and photocatalytic properties under visible light and ultra-violate

نویسنده

  • ,
چکیده مقاله:

In this project, mesoporous titanium oxide-silicon oxide doped by silver (TiO2-SiO2-Ag) was hydrothermally synthesized. Titanium isopropoxide, tetraethyl orthosilicate and silver nitrate were used as precursors for TiO2, SiO2 and Ag, respectively. Initially TiO2-SiO2 mesoporous nanocomposite was synthesized with weight ratios of silica to titania SiO2:TiO2:3:1 via hydrothermal method at 70˚C and 130˚C, then 5wt% of silver was added to each sample. The samples were characterized using XRD, SEM, EDS, Map and BET analysis and photocatalytic performance of synthetic samples under visible light and ultra-violate were investigated using UV-Vis spectroscopy The results of isotherm adsorption-desorption of nitrogen indicate the mesoporous structure of TiO2-SiO2 samples. XRD analysis confirmed the presence of anatase and rutile phases in TiO2-SiO2 samples and also the presence of silver phase along with anatase and rutile in TiO2-SiO2-Ag composition. Examination of the photocatalytic activity of the specimens by visible and ultraviolet light showed that the highest degradation percentage of pollutant (33%) under visible-light and ultra-violate was observed for the sample with silica to titania ratio of 3 via hydrothermal method at 70˚C with additions of silver during synthesis (TS3A-70).

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The Influence of Ag Doping on Structural, Optical Properties and Photocatalytic Activity of TiO2/SiO2 Nanocomposite

In the present study, TiO 2 /SiO 2 and TiO 2 /SiO 2 /Ag nanocomposite powders were synthesized by sol-gel technique. Moreover, for investigation of the Ag doping effect different concentrations of dopant were added. Structures were characterized by IR spectroscopy, Scanning Electron Microscopy (SEM), Energy Dispersive Analytical X-Ray (EDAX), and X-Ray Diffraction (XRD) methods. Fur...

متن کامل

Ag-doped TiO2 Nanocomposite Prepared by Sol Gel Method: Photocatalytic Bactericidal Under Visible Light and Characterization

In  this  reaserch,  photocatalyst  titanium  dioxide  was  doped  with silver  and modified  by  polyethylene  glycol  by  sol  gel method  and the  samples  were  characterized  by  X-ray  diffraction  (XRD)  and scanning  electron  microscopy  (SEM).  The  purpose  of  the  present study  was  to  evaluate  the  photocatalytic  bactericidal  effects  of prepared nanocomposite on human p...

متن کامل

extraction and acetylation of purified trypsin from bovin pancreas and study of some its physico-chemical properties

آنزیم تریپسین در شرایط قلیایی ناپایدار می باشد .و فعالیت پروتئولیتیکی تریپسین منجربه خود هضمی آن در جایگاههای خاصی می گردد. بنابر این آنزیمی با ناپایداری بالا محسوب میگردد. در سالهای اخیر موفق شدند که با ایجاد تغیرات شیمیایی با اضافه کردن فلزات خاص ، کلسیم و یا عمل استیلاسیون منجر به افزایش پایداری آنزیم تریپسین گردند. مطالعات در حال حاضر نشان می دهد که تریپسین استیله شده فعالیت آنزیمی خود را ...

15 صفحه اول

Synthesis of Spongelike Mesoporous Anatase and its Photocatalytic Properties

Mesoporous TiO2 has been prepared using a nonionic block copolymer (Pluronic P-123) as structure-directing agent with sol-gel method. Characterization of the product was carried out by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetry-differential scanning calorimetry (TG-DSC), Nitrogen sorption isotherms, and UV-vis absorpti...

متن کامل

investigation of gassing behavior, electric and dielectric properties of different insulating fluids.

ترانسفورماتورهای قدرت از اجزای اصلی شبکه تامین انرژی الکتریکی می باشند که عملکرد قابل اطمینان ترانسفورماتورها یکی از فاکتورهای مهم و تعیین کننده در تامین انرژی الکتریکی محسوب می شود. در نتیجه بررسی و مانیتور عملکرد ترانسفورماتورها در شبکه و همچنین عیب یابی این ترانسفورماتورها غیرقابل اجتناب و ضروری می باشد. به طور کلی عایق های مایع در صنعت فشار قوی کاربردهای متفاوتی دارند که مهمترین وظیفه آنها...

15 صفحه اول

investigation of the electronic properties of carbon and iii-v nanotubes

boron nitride semiconducting zigzag swcnt, $b_{cb}$$n_{cn}$$c_{1-cb-cn}$, as a potential candidate for making nanoelectronic devices was examined. in contrast to the previous dft calculations, wherein just one boron and nitrogen doping configuration have been considered, here for the average over all possible configurations, density of states (dos) was calculated in terms of boron and nitrogen ...

15 صفحه اول

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 9  شماره 4

صفحات  27- 36

تاریخ انتشار 2021-02

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

کلمات کلیدی برای این مقاله ارائه نشده است

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023