Synthesis of high molecular weight polyethylene using FI catalyst
نویسندگان
چکیده مقاله:
A FI Zr-based catalyst of bis[N-(3,5-dicumylsalicylidene)-2′,6′diisopropylanilinato]zirconium(IV) dichloride was prepared and used for polymerization of ethylene. The effects of reaction conditions on the polymerization were examined in detail. The increase in ethylene pressure and rise in polymerization temperature up to 35 oC were favorable for catalyst/MAO to raise the catalytic activity as well as the viscosity-average molecular weight (Mv) of polyethylene. The activity of the catalyst was linearly increased with increasing MAO concentration and no optimum activity was observed in the range studied. Although introduction of the bulky cumyl and 2′,6′-diisopropyl alkyl substitution groups on ortho positions to the phenoxy-oxygen and on phenyl ring on the N, respectively enhanced the viscosity average molecular weight (Mv) of the obtained polymer strongly, diminished the activity of the catalyst. Neither the activity of the catalyst nor the (Mv) of the obtained polymer were sensitive to hydrogen concentration. However, higher amount of hydrogen could slightly increase the activity of the catalyst. The (Mv) of polyethylene ranged from 2.14×106 to 2.77×106 at the monomer pressure of 3 and 5 bar respectively which are much higher than that of the reported FI Zr-based catalysts.
منابع مشابه
synthesis of high molecular weight polyethylene using fi catalyst
a fi zr-based catalyst of bis[n-(3,5-dicumylsalicylidene)-2′,6′diisopropylanilinato]zirconium(iv) dichloride was prepared and used for polymerization of ethylene. the effects of reaction conditions on the polymerization were examined in detail. the increase in ethylene pressure and rise in polymerization temperature up to 35 oc were favorable for catalyst/mao to raise the catalytic activity as...
متن کاملPreparation of Ultra High Molecular Weight Polyethylene Using Ziegler-Natta Catalyst System: Optimization of Parameters by Response Surface Methodology
متن کامل
Synthesis and Tribological Behavior of Ultra High Molecular Weight Polyethylene (UHMWPE)-Lignin Composites
In this paper, we report the synthesis and characterization of ultra-high molecular weight polyethylene (UHMWPE)-lignin composites. During this study four different compositions, namely UHMWPE, UHMWPE-13 wt. % lignin, UHMWPE-25 wt. % lignin and UHMWPE-42.5 wt. % lignin were fabricated by hot pressing. Detailed microstructural studies by scanning electron microscopy (SEM) showed that UHMWPE and ...
متن کاملProperties of crosslinked ultra-high-molecular-weight polyethylene.
Substantially reducing the rate of generation of wear particles at the surfaces of ultra-high-molecular-weight polyethylene (UHMWPE) orthopedic implant bearing components, in vivo, is widely regarded as one of the most formidable challenges in modern arthroplasty. In the light of this, much research attention has been paid to the myriad of endogenous and exogenous factors that have been postula...
متن کاملsynthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 1 شماره 1
صفحات 25- 32
تاریخ انتشار 2014-01-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023