Surface Degradation of Polymer Matrix Composites Under Different Low Thermal Cycling Conditions
نویسندگان
چکیده مقاله:
The principal effects of mass degradation on polymer matrix composites (PMCs) are the decay of mechanical properties such as strength, elongation, and resilience. This degradation is a common problem of the PMCs under thermal cycling conditions. In this article, composite degradation was investigated by measurement of total mass loss (TML) using the Taguchi approach. Thermal cycling tests were performed using a developed thermal cycling apparatus. Weight loss experiments were performed on the glass fiber/epoxy laminates under different number of thermal cycles and temperature differences. Also, The specimens had various fiber volume fractions and stacking sequences. Statistical analysis is performed to study contribution of each factor. Based on weight loss rates, a regression model was presented to evaluate the TML of laminated composite materials samples. It was found that the temperature differences and fiber volume fraction are the most effective factors of surface degradation with 61 and 22 percent contribution. Also, under the similar experimental conditions, the [0]8 layups exhibits 44 and 35.7 percent more mass loss than the [0/±45/90]s and [02/902]s layups, respectively.
منابع مشابه
surface degradation of polymer matrix composites under different low thermal cycling conditions
the principal effects of mass degradation on polymer matrix composites (pmcs) are the decay of mechanical properties such as strength, elongation, and resilience. this degradation is a common problem of the pmcs under thermal cycling conditions. in this article, composite degradation was investigated by measurement of total mass loss (tml) using the taguchi approach. thermal cycling tests were ...
متن کاملAn Experimental Investigation on Fracture Analysis of Polymer Matrix Composite under Different Thermal Cycling Conditions
Fracture analysis of glass/epoxy composites under different thermal cycling conditions is considered. Temperature difference, stacking sequence, fiber volume fraction and number of thermal cycles are selected as the experimental design factors. The Taguchi method is implemented to design of the experiment and an apparatus is developed for automatic thermal cycling tests. The tensile tests are d...
متن کاملOpen-Hole Size and Thermal Cycling Effects on Mass Loss and Surface Degradation of Polymer Matrix Composites
Degradation is a common problem for polymer matrix composites (PMCs) under low thermal cycling conditions. This paper investigates the effects of low thermal cycling on total mass loss (TML) and surface degradation of PMCs. Unnotched and open-hole specimens were weighed before and after low thermal cycling. The total mass loss and surface degradation of the specimens were studied over 250 cycle...
متن کاملDielectric properties and degradation monitoring in polymer-matrix structural composites
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . xiii CHAPTER
متن کاملBiaxial Yield Surface Investigation of Polymer-Matrix Composites
This article presents a numerical technique for computing the biaxial yield surface of polymer-matrix composites with a given microstructure. Generalized Method of Cells in combination with an Improved Bodner-Partom Viscoplastic model is used to compute the inelastic deformation. The validation of presented model is proved by a fiber Bragg gratings (FBGs) strain test system through uniaxial tes...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 9 شماره 1
صفحات 54- 62
تاریخ انتشار 2017-03-30
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023