Strengthening Mechanisms in the Aged 2024 and 7075 Aluminium Alloys
نویسندگان
چکیده مقاله:
Aluminum 2024 and 7075 alloys which are widely used in aerospace and marine applications were chosen to investigate their strengthening mechanisms. Using differential thermal analysis (DIA), metallography and tension tests, the best solutionizing conditions were determined to be 500±5°C and 2 hours for 2024 and 480?±5°C and 1 hour for 7075 alloy. Aging was performed in the range of 100 to 200°C for various times. It was concluded that the maximum strength in 2024 alloy was developed at l80-190°C after 10 hours and in 7075 alloy at 120°C for 28 hours. In order to determine the strengthening mechanisms in these alloys qualitatively, the T8 treatment (cold work plus aging) was carried out. The results show an increase in the mechanical strength of 2024 alloy whereas the 7075 alloy was not affected appreciably by cold working. It can be concluded that the strengthening mechanism in the 2024 alloy is due to the stress field around the precipitates, whereas in the 7075 alloy it is due to chemical strengthening.
منابع مشابه
Onset Frequency of Fatigue Effects in Pure Aluminum and 7075 (AlZnMg) and 2024 (AlCuMg) Alloys
The viscoelastic response of pure Al and 7075 (AlZnMg) and 2024 (AlCuMg) alloys, obtained with a dynamic-mechanical analyzer (DMA), is studied. The purpose is to identify relationships between the viscoelasticity and fatigue response of these materials, of great interest for structural applications, in view of their mutual dependence on intrinsic microstructural effects associated with internal...
متن کاملAnalysis of Strengthening Mechanisms in an Artificially Aged Ultrafine Grain 6061 Aluminum Alloy
The current study adopted a quantitative approach to investigating the mechanical properties, and their relationship to the microstructural features, of precipitation-strengthened 6061 aluminum alloy processed through accumulative roll bonding (ARB) and aging heat treatment. To serve this purpose, the contributions of different strengthening mechanisms including grain refinement, precipitation...
متن کاملCreep of Aluminium and Aluminium Alloys
This chapter constitutes an introduction to creep and to the creep response of Aluminium and its alloys. Its major goals are: to provide basic information on creep and its mechanisms to give a description of the more extensively used mathematical relations among creep variables (time, stress and temperature) to illustrate the creep response of pure Aluminium and of Al-Mg alloys to provide a syn...
متن کاملNanocrystalline Alloys: Enhanced Strengthening Mechanisms and Mechanically-Driven Structural Evolution
Nanocrystalline materials have experienced a great deal of attention in recent years, largely due to their impressive array of physical properties. In particular, nanocrystalline mechanical behavior has been of interest, as incredible strengths are predicted when grain size is reduced to the nanometer range. The vast majority of research to this point has focused on quantifying and understandin...
متن کاملAn Investigation of the Scatter in Variable - Amplitude Fatigue - Test Results of 2024 and 7075 Materials
SUMMARY The scatter in the fatigue lives of identical simple laboratory specimens, which have been tested under variable amplitude sinusoidal loading, is estimated, using a log-normal distribution of fatigue lives as a basis, from the fatigue test results of a number of experimenters. These estimates of the scatter are analyeed with 8 view to studying the effect of various teat loading paramete...
متن کاملProcessability of high strength Aluminium-Copper alloys AW-2022 and 2024 by Laser Beam Melting in Powder Bed
Additive Manufacturing offers geometric freedom excellently suited for topology optimized light weight designs. Ideally these should be produced from materials of high strength to weight ratio such as aluminium-copper alloys. Yet these are considered unsuitable for welding. With Laser Beam Melting of Metals in powder bed (LBM), the only class of aluminium alloys widely processed is that of alum...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 2 شماره 3
صفحات 144- 151
تاریخ انتشار 1989-11-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023