STRENGTH AND FRACTURE TOUGHNESS OF WHISKER REINFORCED DENTAL RESIN-BASED COMPOSITES
نویسندگان
چکیده مقاله:
Enhancing the properties of dental resin composites is of interest to researchers. The objective of the present investigation was to improve the strength and fracture toughness of dental composites via addition of silicon carbide whiskers and substitution of commonly used filler materials with stabilized zirconia ceramic powder. It was also intended to study the effect of powder- to- whisker ratio on mechanical properties of the resultant composites. The flexural strength and fracture toughness of composite samples with different whiskers loadings were measured. It was found that addition of whiskers to the composites enhances the mechanical properties of the composites. The strength and fracture toughness increased by increasing the amount of whiskers. The flexural strength of a composite having 60wt% whisker and 10wt% zirconia powder was about 210 MPa while that of the composite having only 60wt% ceramic powder was about 110 MPa. The microstructural examinations revealed that reinforcing mechanism was whiskers pull-out as well as crack deflection.
منابع مشابه
Nanoparticle-reinforced resin-based dental composites.
OBJECTIVE TiO(2) nanoparticles treated with the organosilane allyltriethoxysilane (ATES) are used to improve the mechanical properties of dental resin-based composites (RBCs, Z100, 3M ESPE). METHODS TiO(2) nanoparticles were sonically dispersed in an ethanol solution containing ATES. The modified particles were washed in pure ethanol and dried before being used as filler. Fourier transform in...
متن کاملCeramic whisker reinforcement of dental resin composites.
Resin composites currently available are not suitable for use as large stress-bearing posterior restorations involving cusps due to their tendencies toward excessive fracture and wear. The glass fillers in composites provide only limited reinforcement because of the brittleness and low strength of glass. The aim of the present study was to reinforce dental resins with ceramic single-crystalline...
متن کاملFracture toughness, compressive strength and load-bearing capacity of short glass fibre-reinforced composite resin.
OBJECTIVE To investigate the reinforcing effect of short E-glass fibre fillers on fracture related mechanical properties of dental composite resin with a semi-interpenetrating polymer network (IPN) polymer matrix. METHODS Experimental short fibre composite (FC) resin was prepared by mixing 22.5 wt% of short E-glass fibres, 22.5 wt% of IPN-resin and 55 wt% of silane treated silica fillers usin...
متن کاملThe Flexural Strength and Fracture Toughness of TC4-Based Laminated Composites Reinforced with Ti Aluminide and Carbide
TiC-Ti-Al mixed powders and TC4 titanium alloy foils were overlapped layer-by-layer in the graphite die. The TC4-based laminated composite sheets reinforced by Ti aluminide and carbide were successfully fabricated via spark plasma sintering (SPS) at 1100 °C with a well-bonded interface. The composite layers were mainly composed of TiAl, Ti₃Al, Ti₂AlC, and Ti₃AlC₂ phases. The carbides particles ...
متن کاملFracture toughness of dental composites determined using the short-rod fracture toughness test.
Plane strain fracture toughness (KIC) has been evaluated for a number of commercially-available dental composites. A modified Short-rod Fracture Toughness (SRFT) specimen design has been used, enabling small specimens to be tested conveniently. The effect on KIC of aging in water at 37 degrees C for seven days, one month, and six months has been determined for conventional, microfilled, and hyb...
متن کاملFracture Toughness of Polypropylene-Based Particulate Composites
The fracture behaviour of polymers is strongly affected by the addition of rigid particles. Several features of the particles have a decisive influence on the values of the fracture toughness: shape and size, chemical nature, surface nature, concentration by volume, and orientation. Among those of thermoplastic matrix, polypropylene (PP) composites are the most industrially employed for many di...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 2 شماره 4
صفحات 9- 15
تاریخ انتشار 2005-12
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023