Strain and Damage Sensing Property of Self-compacting Concrete Reinforced with Carbon Fibers

نویسندگان

Arvind Cholker Department of Civil Engineering, National Institute of Technology, Srinagar-190006 (J&K), India

Manzoor Tantray Department of Civil Engineering, National Institute of Technology, Srinagar-190006 (J&K), India

چکیده مقاله:

Present paper investigated the strain and damage sensing property on concrete cubes embedded with carbon fibers. Concrete cubes of dimension 150 mm have been casted with different concentration of carbon fibers to study the strain and damage sensing property under cyclic loading that can be further used for health monitoring as non-destructive testing (NDT) approach. All the specimens were tested under cyclic loading within elastic region of the sample for three cycles of loading with a maximum load of 195kN for strain sensing test. During cyclic loading, fractional change in resistance (FCR) is calculated and co-relation with the stress is plotted. During strain sensing test, gauge factors (GF) were also calculated during loading and unloading on the samples. From obtained results, it is found that the concrete sample containing 1.5% of carbon fibers by weight of cement gives best co-relation between stress and FCR that can be further used for health monitoring purpose. Along with strain sensing property, damage sensing property and ultimate load carrying capacities of all the specimens are also reported in present paper with detailed explanation.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Mechanical Behavior of Self-Compacting Reinforced Concrete Including Synthetics and Steel Fibers

This paper investigated the effects of combining fibers with self-consolidating concrete (SCC). 12 series of test specimens were prepared using three kinds of fibers including steel, polyphenylene sulfide (PPS) and glass fibers with four different volumes fractions and one specimen without fibers as a reference sample. All plans were subjected to fresh concrete tests. For mechanical behavior of...

متن کامل

Estimation of mechanical and durability properties of self-compacting concrete with fibers using ultrasonic pulse velocity

In this research, the performance of ultrasonic pulse velocity (UPV) in concrete is examined as a nondestructive experiment in order to estimate mechanical (compressive and tensile strength) and durability (water absorption) properties of fiber-reinforced self-compacted concrete For this purpose 11 mixture designs containing 3 types of fibers (steel: 0.1, 0.2, 0.3 and 0.4 percent by volume, Pol...

متن کامل

mechanical behavior of self-compacting reinforced concrete including synthetics and steel fibers

this paper investigated the effects of combining fibers with self-consolidating concrete (scc). 12 series of test specimens were prepared using three kinds of fibers including steel, polyphenylene sulfide (pps) and glass fibers with four different volumes fractions and one specimen without fibers as a reference sample. all plans were subjected to fresh concrete tests. for mechanical behavior of...

متن کامل

Strength and Toughness of Reinforced Concrete with Coated Steel Fibers

The effect of zinc phosphate (ZP) and zinc calcium phosphate (ZCP) coatings on the reinforcing mechanisms of smooth steel fiber in cementitious matrix have been studied. The results of pull out tests illustrated that by coating smooth steel fiber the pull-out load may be increased up to 100%. The effect of zinc phosphate coating on interface bonding was more than zinc-calcium phosphate coating....

متن کامل