Preparation and Characterization of Tetragonal Zirconium Oxide Nanocrystals from Isophthalic Acid-Zirconium(IV) Nanocomposite As a New Precursor
نویسندگان
چکیده مقاله:
In this study, isophthalic acid-zirconium(IV) nanocomposite has been prepared from zirconyl nitrate pentahydrate and potassium iodide, with isophthalic acid, (C8H6O4=Benzene-1,3-dicarboxylic acid) as a ligand, via sonochemical method in ethylene glycol and methanol as solvents. The crystalline tetragonal ZrO2 has been produced by thermal decomposition of isophthalic acid-zirconium(IV) nanocomposite as precursor. Characterization of nanocomposite was carried out using element analysis, Fourier transfer infrared spectroscopy (FT-IR), X-ray powder diffraction (XRD), scanning electron microscopy (SEM) and thermal gravimetric analysis (TGA) techniques. The results demonstrated that, pure zirconia with particle size of about 49 nm was obtained in which methanol has been used as solvent during the reaction, particle sizes was significantly reduced to about 20 nm, when ethylene glycol used as solvent during formation of the nanocomposite isophthalic acid-zirconium (IV) as precursor.
منابع مشابه
preparation and characterization of tetragonal zirconium oxide nanocrystals from isophthalic acid-zirconium(iv) nanocomposite as a new precursor
in this study, isophthalic acid-zirconium(iv) nanocomposite has been prepared from zirconyl nitrate pentahydrate and potassium iodide, with isophthalic acid, (c8h6o4=benzene-1,3-dicarboxylic acid) as a ligand, via sonochemical method in ethylene glycol and methanol as solvents. the crystalline tetragonal zro2 has been produced by thermal decomposition of isophthalic acid-zirconium(iv) nanocompo...
متن کاملSynthesizing and Characterization of Monoclinic and Tetragonal Phases of Zirconium Oxide (Zro2) Nanofibers with the Aid of Electrospinning Technique
Zirconium oxide has found extensive applications in various industries becauseof its excellent properties such as high strength; high-temperature resistance;extraordinary wearing resistance; ionic conductivity; and corrosion resistance. Also, someProperties like high melting point, high mechanical and thermal strength, high dielectricconstant and low conductivity have in...
متن کاملProcessing and Characterization of Cellulose Nanocrystals/Polylactic Acid Nanocomposite Films
The focus of this study is to examine the effect of cellulose nanocrystals (CNC) on the properties of polylactic acid (PLA) films. The films are fabricated via melt compounding and melt fiber spinning followed by compression molding. Film fracture morphology, thermal properties, crystallization behavior, thermo-mechanical behavior, and mechanical behavior were determined as a function of CNC co...
متن کاملPreparation of Cobalt Oxide/Zinc Oxide Nanocomposite
Cobalt Oxide/ Zinc Oxide nanocomposite was synthesized by dropwise addition ofCo(NO)3.6H2O and Zn(NO3)2.4H2O solutions to KOH solution at different temperatures followed bycalcination at 300ºC for 4 h. The morphology and structure of nanoparticles and the influence oftemperature on particle size were studied using scanning electron microscopy (SEM) and X-RayDiffraction (XRD). Minimum particle s...
متن کاملPreparation and characterization of hydroxyapatite reinforced with hardystonite as a novel bio-nanocomposite for tissue engineering
Objecttive(s): Despite the poor mechanical properties of hydroxyapatite, its unique biological properties leads we think about study on improving its properties rather than completely replacing it with other biomaterials. Accordingly, in this study we introduced hydroxyapatite reinforced with hardystonite as a novel bio-nanocompositeand evaluate its in-vitro bioactivity with the aim of developi...
متن کاملPreparation and Characterization of a Cotton-Based Nanocomposite Hydrogel
In this work, hydrogel nanocomposites were synthesized by solution polymerization of acrylic acid (AA) and itaconic acid (IA) in the presence of cotton fabric. Ammonium persulfate (APS) was used as the polymerization initiator in the presence of a crosslinker, methylene bisacrylamide (MBA). Insertion of Ag followed by reduction of Ag+ cations results in a hydrogel nanocomposite. The ...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 8 شماره 4
صفحات 191- 196
تاریخ انتشار 2012-12-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023