Palladium composite membrane with high reversibility of CO2 poisoning
نویسندگان
چکیده مقاله:
A palladium membrane was prepared using the electroless plating technique (ELP) for the separation and purification of hydrogen from a gas mixture. Depending on operating conditions, hydrogen flux from the membrane was in the range of 0.012-0.023 mol.m-2.s-1. The membrane performance in the presence of CO2 was investigated. The results of the GC analysis showed that at a feed concentration of 10% CO2 and a difference pressure of 1-2 bar, no traces of CO2 was observed in the permeate side. However, hydrogen permeation through the membrane decreased due to the occupation of the catalytic active sites by CO2.. At the concentration of 20% CO2 and a difference pressure of 1-2 bar, a peak of methane was detected in the permeate side by the GC analysis, this is related to the diffusion of carbon from the feed side to the permeation side. Study on the topography of the membrane surface showed short height hills and wide valleys on its surface. This topology of the surface conduced high chemical resistance of the membrane, so that the effect of CO2 poisoning was reversible without defect creation on the membrane. Recovery of the poisoned membrane was done by exposing it to hydrogen atmosphere at 500 °C for an hour. The obtained results show that the recovery of hydrogen permeation was up to 99%.
منابع مشابه
Novel Electroless Plating of Ruthenium for Fabrication of Palladium-Ruthenium Composite Membrane on PSS Substrate and Its Characterization
This paper focused on a novel method of electroless plating ruthenium (Ru) on solid or porous substrates like porous stainless steel (PSS) discs or ceramic tubes. A novel complexing plating bath of Ru was developed. It is proven that Ru can be deposited directly on these substrates by the bath at a temperature of 328 K and strong alkaline environment. TGA, SEM, EDX and XRD confirmed the success...
متن کاملComposite electrolyte membranes for high temperature CO2 separation
Amembrane device that can selectively separate CO2 at temperatures exceeding 600 ◦C has been demonstrated. The membrane can be made from a composite material made of a molten carbonate electrolyte eceived in revised form 24 October 2010 ccepted 28 October 2010 vailable online 3 November 2010
متن کاملCorrelating Physicochemical Properties of Commercial Membranes with CO2 Absorption Performance in Gas-Liquid Membrane Contactor
The gas-liquid membrane contactor (GLMC) is a promising alternative gas absorption/desorption configuration for effective carbon dioxide (CO2 ) capture. The physicochemical properties of membranes may synergistically affect GLMC performances, especially during the long-term operations. In this work, commercial polypropylene (PP) and polyvinylidene fluoride (PVDF) hollow fiber (HF) membranes wer...
متن کاملnovel electroless plating of ruthenium for fabrication of palladium-ruthenium composite membrane on pss substrate and its characterization
this paper focused on a novel method of electroless plating ruthenium (ru) on solid or porous substrates like porous stainless steel (pss) discs or ceramic tubes. a novel complexing plating bath of ru was developed. it is proven that ru can be deposited directly on these substrates by the bath at a temperature of 328 k and strong alkaline environment. tga, sem, edx and xrd confirmed the success...
متن کاملEnhanced stability of membrane reactor for thermal decomposition of CO2 via porous-dense-porous triple-layer composite membrane
A triple-layer composite membrane with porous-dense-porous structure was proposed to develop a high performance membrane reactor. The triple-layer composite membrane consists of a porous Sr0.7Ba0.3Fe0.9Mo0.1O3 δ (SBFM) layer, a dense 0.5 wt% Nb2O5-doped SrCo0.8Fe0.2O3 δ (SCFNb) layer and a porous La0.8Sr0.2MnO3 δ–yttria stabilized zirconia (LSM/YSZ) layer. The porous layers can effectively redu...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 5 شماره 1
صفحات 13- 19
تاریخ انتشار 2018-08-25
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023