OPTICAL ABSORPTION IN Ce0 -V 0 EVAPORATE THIN FILMS
نویسندگان: ثبت نشده
چکیده مقاله:
In this work, the optical absorption near the fundamental absorption edge of co-evaporated Ce0 -V20 films is studied. It is found that the fundamental optical absorption in these materials is sharp more like that expected for crystals. It is also found that as the V O content increases, the edge becomes less sharp and shifts towards higher wavelengths
منابع مشابه
OPTICAL PROPERTIES OF CO-EVAPORATED THIN FILMS OF BINARY Bi 0-Te 0 AND Bi 0 -V 0 SYSTEMS
Thin films of binary Bi 0 -TeO and Bi 0 -V 0 systems were prepared by the thermal co-evaporation technique in a vacuum at room temperature. The optical absorption edge of these systems are studied in the wavelength of 200-800 nm using a PERKIN-ELMER uv/Vis spectrophotometer. It is found that the value of n=3/2 in the Davis-Mott equation is best fitted for the fundamental absorption edge f...
متن کاملoptical properties of co-evaporated thin films of binary bi 0-te 0 and bi 0 -v 0 systems
thin films of binary bi 0 -teo and bi 0 -v 0 systems were prepared by the thermal co-evaporation technique in a vacuum at room temperature. the optical absorption edge of these systems are studied in the wavelength of 200-800 nm using a perkin-elmer uv/vis spectrophotometer. it is found that the value of n=3/2 in the davis-mott equation is best fitted for the fundamental absorption edge for the...
متن کاملFabrication of Nb/V co-doped TiO2 thin films and study of structural, optical and photocatalytic properties
In this study, different samples of Niobium and Vanadium co-doped titania thin films (5-10-15 mol% Nb and 5-10-15 mol% V) were prepared via sol−gel dip coating method, using niobium chloride as niobium precursor, ammonium metavanadate as vanadium precursor, and titanium (IV) butoxide (TBT) as titanium precursor. The effects of doping amount on the structural, optical, and photo-catalytic prope...
متن کاملFabrication of Nb/V co-doped TiO2 thin films and study of structural, optical and photocatalytic properties
In this study, different samples of Niobium and Vanadium co-doped titania thin films (5-10-15 mol% Nb and 5-10-15 mol% V) were prepared via sol−gel dip coating method, using niobium chloride as niobium precursor, ammonium metavanadate as vanadium precursor, and titanium (IV) butoxide (TBT) as titanium precursor. The effects of doping amount on the structural, optical, and photo-catalytic prope...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملOptical Metrology of Thin Films
A non-contact and non-destructive laser-based acoustic technique called impulsive stimulated thermal scattering (ISTS) is demonstrated for new applications in the context of a compact, portable apparatus. ISTS is used to determine viscoelastic and thermal transport properties of a DuPont Kapton film before and after neutron irradiation to determine the changes that would be expected to occur in...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 5 شماره 2
صفحات -
تاریخ انتشار 1994-09-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023