Microstructure and mechanical properties of similar and dissimilar welding joints of weathering steel and plain carbon steel by GMAW with CO2 shielding gas
نویسندگان
چکیده مقاله:
The welding joints were investigated due to the significance of similar welding of Corten A weathering steel and its dissimilar welding with St12 plain carbon steel in industrial applications. The gas metal arc welding (GMAW) technique with carbon dioxide shielding gas was utilized in the present work. The welding process comprised current and voltage control, welding wire injection rate, shielding gas rate, welding speed, connection configuration, and microstructure evolution. Mechanical properties and microstructure evolution in similar and dissimilar joints and weld defects were evaluated by tensile, bending, hardness, metallographic, and radiographic tests. The weld microstructure in similar and dissimilar joints included grain boundary ferrite, acicular ferrite, and WidmanStatten ferrite. The tensile strengths of the similar and dissimilar joints were respectively 497 and 303 MPa. The weld zone hardness was 210 and 180 Vickers for similar and dissimilar joints, respectively. In conclusion, similar welding outperformed dissimilar welding considering weld joint defects, mechanical properties, and microstructure.
منابع مشابه
Gas tungsten arc welding of direct quenched wear resistant steel to plain carbon steel and evaluation of its microstructure and wear properties
In this research, the dissimilar welding of St52 plain carbon steel to W400 wear resistant steel and its effect on the microstructure and wear properties of the wear resistant steel was investigated. The wear resistant steel was produced via direct quenching with nominal hardness of 400 HB. Gas tungsten arc welding was used for joining process. The results showed that welding led to hardness re...
متن کاملGas tungsten arc welding of direct quenched wear resistant steel to plain carbon steel and evaluation of its microstructure and wear properties
In this research, the dissimilar welding of St52 plain carbon steel to W400 wear resistant steel and its effect on the microstructure and wear properties of the wear resistant steel was investigated. The wear resistant steel was produced via direct quenching with nominal hardness of 400 HB. Gas tungsten arc welding was used for joining process. The results showed that welding led to hardness re...
متن کاملdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولEvaluation of microstructure and mechanical properties of friction stir welded copper / 316L stainless steel dissimilar metals
In the present research, friction stir welding (FSW) process was used for butt joining of pure copper plate to 316L stainless steel plate. Mechanical properties and microstructural characteristics of the joint were evaluated by microhardness and tensile tests as well as optical and scanning electron microscope (SEM). It was found that microstructure of the weld nugget (WN) has fine grains where...
متن کاملEffect of Welding Parameters in the Microstructure and Mechanical Properties of Friction-Welded Joints of 100Cr6 Steel
In this study, high-carbon, chromium alloy steel (100Cr6) having the initial spheroidized microstructure was welded using the rotary friction welding method. The effects of process parameters such as friction time and friction force were experimentally investigated. The friction welded joints were produced of two 100Cr6 steel rods. In order to examine the microstructure and mechanical properti...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 8 شماره 1
صفحات 17- 27
تاریخ انتشار 2022-08
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023