Microleakage under Orthodontic Metal Brackets Bonded with Three Different Bonding Techniques with/without Thermocycling
نویسندگان
چکیده مقاله:
Introduction: The aim of this study was to compare the microleakage of beneath the orthodontic brackets bonded with 3 different bonding techniques and evaluate the effect of thermocycling. Methods: One hundred and twenty premolars were randomly divided into 6 groups, received the following treatment: group 1: 37% phosphoric acid gel+Unite primer+Unite adhesive, group 2: 37% phosphoric acid gel+ Transbond XT primer+Transbond XT adhesive, group 3: Transbond plus Self Etching Primer (TSEP)+Transbond XT adhesive. Groups 4, 5, and 6 were similar to groups 1, 2, and 3, respectively. Evaluation of microleakage was done following to thermocycling test. After bonding, the specimens were sealed with nail varnish except for 1 mm around the brackets and then stained with 0.5% basic fuchsine. The specimens were sectioned at buccolingual direction in 2 parallel planes and evaluated under a stereomicroscope to determine the amount of microleakage at bracket-adhesive and adhesive-enamel interfaces from gingival and occlusal margins. Results: Microleakage was observed in all groups, and increased significantly after thermocycling at some interfaces of Unite adhesive group and conventional etching+Transbond XT adhesive group, but the increase was not significant in any interface of TSEP group. With or without thermocycling, TSEP displayed more microleakage than other groups. In most groups, microleakage at gingival margin was significantly higher than occlusal margin. Conclusion: Thermocycling and type of bonding technique significantly affect the amount of microleakage.
منابع مشابه
microleakage under orthodontic metal brackets bonded with three different bonding techniques with/without thermocycling
introduction: the aim of this study was to compare the microleakage of beneath the orthodontic brackets bonded with 3 different bonding techniques and evaluate the effect of thermocycling. methods: one hundred and twenty premolars were randomly divided into 6 groups, received the following treatment: group 1: 37% phosphoric acid gel+unite primer+unite adhesive, group 2: 37% phosphoric acid gel+...
متن کاملMicro-CT evaluation of microleakage under orthodontic ceramic brackets bonded with different bonding techniques and adhesives.
AIM The aim of this study was to evaluate microleakage under orthodontic ceramic brackets bonded with direct and different indirect bonding techniques and adhesives using micro-computed tomography. MATERIALS AND METHODS A total of 30 human maxillary premolars were randomly separated into five groups with six teeth in each group. In group I, teeth were bonded directly with Transbond XT (3M Uni...
متن کاملMicroleakage under orthodontic brackets bonded with different adhesive systems
OBJECTIVE This in vitro study aimed to compare the microleakage of orthodontic brackets between enamel-adhesive and adhesive-bracket interfaces at the occlusal and gingival margins bonded with different adhesive systems. MATERIALS AND METHODS A total of 144 human maxillary premolar teeth extracted for orthodontic reasons was randomly divided into four groups. Each group was then further divid...
متن کاملMicroleakage under orthodontic brackets bonded with the custom base indirect bonding technique.
The aim of this in vitro study was to compare microleakage of orthodontic brackets between enamel-composite and composite-bracket interfaces at the occlusal and gingival margins, bonded using indirect bonding systems with that of a conventional direct bonding method. Forty freshly extracted human maxillary premolar teeth were randomly divided into two groups. In group 1, the brackets were bonde...
متن کاملMicroleakage beneath brackets bonded with flowable materials: effect of thermocycling.
The purpose of this study was to evaluate the effects of thermocycling on microleakage beneath brackets bonded with an orthodontic composite and different flowable materials. Brackets were bonded to 200 bovine incisors divided into five groups: (1) Transbond XT, (2) X-Flow, (3) Dyract-Flow, (4) Admira-Flow, and (5) Beautiful-Flow. Half the teeth in each group were thermocycled. The specimens we...
متن کاملThe effect of different surface treatments of demineralised enamel on microleakage under metal orthodontic brackets
BACKGROUND The aim of this investigation was to assess the effects of different treatments of demineralised enamel on microleakage under orthodontic brackets. METHODS Seventy-five intact premolars were randomly assigned to five groups. The teeth in groups 2 through 5 were immersed in a demineralising solution for 16 weeks. In groups 1 (control) and 2 (demineralised/control), conventional acid...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 2 شماره 1
صفحات 21- 28
تاریخ انتشار 2013-03-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023