Influence of Initial Microstructure on Hot Deformation Behavior of Duplex Stainless Steels
نویسندگان
چکیده مقاله:
In this research the effect of initial microstructure on hot deformation behavior in terms of Ferrite-to-Austenite ratios is studied. Two types of stainless steels C1 and C2 were homogenizing heat-treated and deformed under hot compression examinations at temperatures 900ºC and 1100ºC at strain rate of 0.1s-1. The results showed that the flow stress levels of specimens are strongly related to deformation parameters and initial microstructures of steels. Moreover, during cooling from 1350ºC to the deformation temperature, flow stress level increased for both samples because of increment in austenite content.
منابع مشابه
Influence of Boron on Initial Austenite Grain Size and Hot Deformation Behavior of Boron Microalloyed Steels
The initial austenite grain size of boron microalloyed steel with three different amounts of boron (20, 40, and 60 ppm) was investigated under different heating temperatures (1150, 1100, and 1050 °C), and hot compression tests of samples in a wide range of temperature (900–1100 °C) and strain rate (0.1–10 s−1) were conducted. It was found that the initial austenite grain size increases with inc...
متن کاملEffects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. 
The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite r...
متن کاملEffects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite reg...
متن کاملSuper Plasticity of /α Duplex Stainless Steels
In this paper the studies of the two-phase super Plasticity stainless steels is studied. The aim of this study obtained the suitable criteria to thermo-mechanical treatment condition for decrease the microstructure (grain size) and super plasticity property in two-phase stainless steels. Also here we want to show the appropriate ranges of temperature and strain rate used in the process super pl...
متن کاملHot Deformation Behavior of 17-7 PH Stainless Steel
To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملeffects of carbon on the microstructure and hot deformation behavior
the effects of carbon content on the dynamic and static softening mechanisms of ti microalloy steels were investigated both in ferrite and austenite regions. the results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. this is due to the ti(cn) and tic precipitates and also the free carbon content. in the ferrite regio...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 1 شماره 2
صفحات 61- 67
تاریخ انتشار 2013-04-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023