Growth, corrosion, and wear study of nanocomposite PEO coating in electrolyte containing nickel sulfate
نویسندگان
چکیده مقاله:
Plasma electrolytic oxidation (PEO) was performed on a 1010 Aluminum alloy. To achieve thenanocomposite structure, Si3N4 nanoparticles were added into the electrolyte. In an alkaline aqueoussuspension (silicate-based), the effect of adding NiSO4 on the applied voltage, microstructure,composition, wear, and corrosion resistance of PEO coatings was investigated using ScanningElectron Microscopy (SEM), elemental analysis with Energy Dispersive Spectroscopy (EDS), X-RayDiffraction (XRD), cyclic polarization test, and pin-on-disk wear test. The results showed that addingnickel sulfate (NiSO4) and infiltration of its constituents into coatings lead to a more favored corrosionbehavior. Moreover, in the case of best sample, anodic current at the highest applied potentialcondition during the cyclic polarization test indicated a drop within two decades. Moreover,coefficient of friction decreased almost by half.
منابع مشابه
growth, corrosion, and wear study of nanocomposite peo coating in electrolyte containing nickel sulfate
plasma electrolytic oxidation (peo) was performed on a 1010 aluminum alloy. to achieve thenanocomposite structure, si3n4 nanoparticles were added into the electrolyte. in an alkaline aqueoussuspension (silicate-based), the effect of adding niso4 on the applied voltage, microstructure,composition, wear, and corrosion resistance of peo coatings was investigated using scanningelectron microscopy (...
متن کاملSYNTHESIS AND STUDY OF CORROSION PERFORMANCE OF EPOXY COATING CONTAINING MULTI-WALLED CARBON NANOTUBE/ POLY ORTHO AMINOPHENOL NANOCOMPOSITE
The epoxy coatings containing multi-walled carbon nanotube/ poly ortho aminophenol nanocomposite were prepared and used as anticorrosive coatings. The nanocomposites with different contents of carbon nanotube were synthesized in a solution of sodium dodecyl sulfate and ammonium peroxy disulfate as a surfactant and an oxidant, respectively. The morphology and structural properties were confirmed...
متن کاملElectrochemical Evaluation of Polyvinyl Butyral Coating Containing Polypyrrole/ZnO Nanocomposite for Corrosion protection of Al Alloy
In this work, polypyrrole/ZnO nanocomposite (PPy/ZnO NC) was produced through synthesis of polypyrrole polymer in the presence of ZnO nanoparticles. The corrosion behavior of polyvinyl butyral coatings without and with different weight percentages of nanocomposite on the surface of 7075 Al alloy was investigated in 3.5% NaCl solution at different immersion times using electrochemical impedance ...
متن کاملan investigation about the relationship between insurance lines and economic growth; the case study of iran
مطالعات قبلی بازار بیمه را به صورت کلی در نظر می گرفتند اما در این مطالعه صنعت بیمه به عنوان متغیر مستفل به بیمه های زندگی و غیر زندگی شکسته شده و هم چنین بیمه های زندگی به رشته های مختلف بیمه ای که در بازار بیمه ایران سهم قابل توجهی دارند تقسیم میشود. با استفاده از روشهای اقتصاد سنجی داده های برای دوره های 48-89 از مراکز ملی داده جمع آوری شد سپس با تخمین مدل خود بازگشتی برداری همراه با تعدادی ...
15 صفحه اولErosion-corrosion and wear
The basic processes of wear, erosion and erosion-corrosion are reviewed. It is shown that oxide debris can accelerate wear when it is present as particulates, or protect and reduce friction when it is present as a glaze. Erosion-corrosion processes can be understood and organized in a series of regimes that represent a sequence of change in the relative intensities of erosive and corrosive proc...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 48 شماره 2
صفحات 133- 144
تاریخ انتشار 2015-12-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023