Grain growth kinetic of spark plasma sintered magnesia
نویسنده
چکیده مقاله:
In this research, the densification of magnesia nanopowder with a mean particle size of about 100 nm was investigated by spark plasma sintering undera pressures of 80 MPa and at temperature range from 1000 °C to 1400 °C and a heating rate of 50 °C/min for 20 minutes. The density of the samples slowly increased with increasing sintering temperatures to 1200 °C. Afterwards, with more increasing of temperature, decreasing density and increasing of grain growth were observed. Grain growth was analyzed during the sintering process with the classic grain growth theory. The results of the survey on the density showed that the highest densification rate occurred at 1100 ℃. The activation energy of grain growth was Obtained 452.24 kJ / mol. The MgO ceramic spark plasma sintered at 1200 °C for 20 min demonstrated the highest infrared transmittance of 67 % at the 5.6 μm wavelength.
منابع مشابه
Microstructure of spark plasma sintered TiB2 and TiB2–AlN ceramics
In this research study, the effects of aluminum nitride (AlN) additive on the densification behavior and microstructure development of titanium diboride (TiB2) based ceramic matrix composite were investigated. In this way, a monolithic TiB2 ceramic and a TiB2–5 wt% AlN ultrahigh temperature ceramic composite were fabricated by spark plasma sintering (SPS) proces...
متن کاملMicrostructure and Properties of Spark Plasma Sintered MoAlB Ceramics
Advisor: Bai Cui Molybdenum aluminum boride (MoAlB) is a ternary transition metal boride which has promising aeronautic and nuclear applications. It inheres excellent properties of the binary transitional metal borides (e.g., MoB, ZrB2) such as high melting temperature, high hardness, and thermal conductivity. Besides, MoAlB is superior to MoB because: (1) the Al element provides an oxidation r...
متن کاملRadiation Stability of Spark-Plasma-Sintered Lead Vanadate Iodoapatite
Fengyuan Lu, Tiankai Yao, Yaron Danon, Jianren Zhou, Rodney C. Ewing, and Jie Lian Department of Mechanical and Industrial Engineering, Louisiana State University, Baton Rouge, Louisiana 70803 Department of Mechanical, Aerospace, and Nuclear Engineering, Rensselaer Polytechnic Institute, Troy, New York 12180 Department of Geological & Environmental Sciences, Stanford University, Stanford, Calif...
متن کاملStability of Nanocrystalline Spark Plasma Sintered 3Y-TZP
Spark plasma sintered 3Y-TZP has been investigated with respect to hydrothermal ageing and grinding. The sintering was performed between the temperatures of 1,100 and 1,600 °C for a soaking time of 5 minutes and the resulting materials were obtained with grain sizes between 65 to 800 nm and relative densities between 88.5 to 98.8%. Experiments on hydrothermal ageing in water vapour at 131 °C, 2...
متن کاملMicrostructure of Spark Plasma-Sintered Silicon Nitride Ceramics
The microstructure and phase composition of the high-content Al2O3-Y2O3-doped spark plasma-sintered silicon nitride were investigated. Fully dense silicon nitride ceramics with a typical α-Si3N4 equiaxed structure with average grain size from 200 to 530 nm, high elastic modulus of 288 GPa, and high hardness of 2038 HV were spark plasma sintered (SPSed) at 1550 °C. Silicon nitride with elongated...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 8 شماره 4
صفحات 29- 42
تاریخ انتشار 2020-02
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023