Grafting of Maleic Anhydride onto Co)propylene-b-ethylene( by Extrusion Process: Measurement of Adhesion to Steel Surface
نویسندگان
چکیده مقاله:
Polypropylene (PP) has poor adhesion to metals and other surfaces for its chemical structure. Hence, chemical modification of PP is necessary for metal surface coating application. In this research, grafting of maleic anhydride (MA) onto co(propylene-b-ethylene) in the presence of a dicumyl peroxide (DCP) was accomplished in a single screw extruder. Characteristics of the modified polymer were determined by Infra-red Spectroscopy (IR), Scanning Electron Microscopy (SEM), and adhesion test. Maximum grafting of MA was found to be 1.2832% for 1.5 pph of MA. Adhesion test showed that the samples containing 1 pph of MA (degree of grafting is 0.5816%) had better adhesion to steel surface (17.25 kgf).
منابع مشابه
Grafting of Tetrahydrophthalic and Maleic Anhydride Onto Polyolefins in Solution
Polietileno de baixa densidade (LLDPE) com comonômeros 1-buteno e 1-octeno foram funcionalizados com anidrido tetrahidroftálico (THA) e anidrido maléico (MA) em solução na presença de peróxido de benzoíla (BPO), de acordo com planejamentos fatoriais. As variáveis testadas foram concentração de anidrido, concentração de peróxido, tempo de reação e tipo de comonômero. As formulações foram analisa...
متن کاملComparison of grafting of maleic anhydride onto linear low density polyethylene with hexene-1 and butene-1 comonomers and prediction of optimum ingredients by response surface methodology
In this work, the grafting of maleic anhydride onto two types of linear low density polyethylene with hexene-1 comonomer (LLDPE-H1) and butene-1 comonomer (LLDPE-B1), in the presence of styrene monomer (St) and dicumyl peroxide initiator (DCP) has been studied. The combined influences of MAH, St and DCP on the grafting efficiency via a melt reactive mixing process have been investigated using r...
متن کاملMelt Free-Radical Grafting of Maleic Anhydride onto Biodegradable Poly(lactic acid) by Using Styrene as a Comonomer
Maleic anhydride (MA) was grafted onto poly(lactic acid) (PLA) in the presence of styrene (St) by using a free-radical grafting methodology. The grafting degree (Dg) of MA was increased from 0.65 wt % to 1.1 wt % with the St/MA ratio up to 2/1, where the grafting efficiency (Eg) of MA was 27%. However, both Dg and Eg were decreased with further increasing of the St/MA ratio to 4/1. The Dg of MA...
متن کاملMechanical Properties of Polypropylene Coating Containing Maleic Anhydride on Plain Carbon Steel
Using Electrostatic Spray Coating Technique, Polypropylene Powder (EPD 60R) was applied on carbon steel substrates at room temperature. In order to obtain a uniform coating, steel substrates with powder coatings were heated in a vacuum oven at various temperatures up to 250° C for various periods of time up to 45 min and a pressure of 200 mb. The coatings produced had thicknesses of around 470 ...
متن کاملMechanical Properties of Polypropylene Coating Containing Maleic Anhydride on Plain Carbon Steel
Using Electrostatic Spray Coating Technique, Polypropylene Powder (EPD 60R) was applied on carbon steel substrates at room temperature. In order to obtain a uniform coating, steel substrates with powder coatings were heated in a vacuum oven at various temperatures up to 250° C for various periods of time up to 45 min and a pressure of 200 mb. The coatings produced had thicknesses of around 470 ...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 26 شماره 1
صفحات 313- 322
تاریخ انتشار 2007-07
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023