Fe-Loaded CeO2 Nanosized Prepared by Simple Co-Precipitation Route
نویسندگان
چکیده مقاله:
FeCe nanoparticles were synthesized by simple co-precipitation method using Iron chloride hexahydrate (FeCl3.6H2O) and cerium chloride (CeCl2•5H2O) as precursors in the presence of cetyltrimethylammonium bromide (CTAB) surfactant. The samples were characterized by high resolution transmission electron microscopy (HRTEM), field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), vibration sampling magnetometer (VSM), electron dispersive spectroscopy (EDS) and Fourier transform infrared spectroscopy (FTIR) at different temperatures. The XRD results showed that Fe-doped CeO2 was single-phased with a cubic structure. SEM images showed the rod-shaped particles of as-prepared sample in the range size of 40-80 nm and annealed smallest one around 15 nm in diameter at 500oC for 3 h. The TEM studies revealed the squared-like shaped nanosized particles. The sharp peaks in the FTIR spectrum determined the element of Fe-Ce nanoparticles. The EDS spectra showed peaks of iron and cerium with less impurity in the prepared samples. The result of magnetic measurements showed a coercive field and saturated magnetization around 1650 G and 0.04 emu/g for as-prepared samples, respectively.
منابع مشابه
CTAB-assisted of Fe2O3/CeO2 nanosized prepared by coprecipitation method
Recently, cerium oxide (CeO2) nanoparticles have been widely used in engineering andmedical sciences due to the diversity of their applications. Fe-Ce nanoparticles were synthesized bysimple co-precipitation method via iron nitrate (Fe(NO3)3.9H2O) and cerium nitrate (Ce(NO3)3.6H2O) asprecursor in the presence of cetyltrimethylammonium bromide (CTAB) surfactant. The samples wer...
متن کاملSynthesis of Fe-doped CeO2 Nanoparticles Prepared by Solgel Method
Nanomaterials have achieved remarkable technological advances in bulk materials due to their excellent physical, chemical and biological properties. cerium oxide (CeO2) nanostructured doped with Fe ions is attractive due to improvement in redox properties, transport property and surface-to-volume ratio. In this research, Fe-doped CeO2 nanoparticles (NPs) were prepared by s...
متن کاملNanosized strontium aluminate phosphors prepared via a reverse microemulsion route
Nanosized strontium aluminate phosphors co-activated by Eu2+ and Dy3+ were prepared via a novel reverse microemulsion process. This new ynthesis technique lowered the synthesis temperature of SrAl2O4: Eu2+, Dy3+ phosphors to as low as 900 ◦C, and also reduced the particle size o the nanometer scale (around 40 nm). In the microemulsion process, the constituent cations were trapped by numerous na...
متن کاملStructure and Magnetic Properties of Oxide Nanoparticles of Fe-Co-Ni Synthesized by Co-Precipitation Method
Oxide nanoparticles of Fe-Co-Ni were prepared in six different compositions by co-precipitation method. The as-synthesized nanoparticles were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron microscope (FESEM), Fourier Transform Infrared (FT-IR) and Vibrating Sample Magnetometer (VSM). It was found that the nanoparticles had mean crystalline size of 30-55 nm and spher...
متن کاملCharacterization of the metastable Cu-Fe nanoparticles prepared by the mechanical alloying route
Although Cu and Fe are immiscible under equilibrium conditions, they can form supersaturated solid solutions by mechanical alloying. In this paper, nano-structured of the metastable Cu-Fe phase containing 10, 15, 20 and 25% wt Fe were synthesized by intensive ball milling for 15h, in order to achieve a solid solution of Fe in Cu. The phase composition, dissolution of the Fe atoms into the Cu ma...
متن کاملSimple Route to Obtain Nanostructured CeO2 Microspheres and CO Gas Sensing Performance
In this work, nanostructured CeO2 microspheres with high surface area and mesoporosity were prepared by the coprecipitation method, in absence of a template. The reaction between cerium nitrate and concentrated formic acid produced cerium formate, at room temperature. Further, calcination at 300 °C yielded single-phase CeO2 microspheres, with a diameter in the range 0.5-2.6 μm, the surface of t...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 6 شماره 4
صفحات 713- 720
تاریخ انتشار 2018-12-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023