Evaluation of Microstructure and Wear Behavior of Iron-based Hard - facing Coatings on the Mo40 Steel
نویسندگان
چکیده مقاله:
Mo40 low-alloy steels are mostly used to produce industrial components such as crane wheels which are exposed to abrasive wear. However, during working conditions, their wear resistance is reduced after a while due to its low hardness. With increasing abrasive wear, the dimensions of components decrease and they need to be repaired for surface modification. In this regard, hard overlay coatings are applied by hard-facing process for reusing these components. This work deals with the surface analysis, hardness and wear behaviors of the clad layers made of the Fe-Cr-C based hard-facing on the Mo40 low-alloy steel by submerged arc welding method. The overlay coatings are performed by two ways of welding: 1. rods of UP6-GF-50 (307 kavosh joosh standard number), and 2. UP6-GF-50-C (420 kavosh joosh standard number) regarding the Din 8555 standard, in single and double passes. According to the X-ray diffraction analysis and microstructure characteristics, both martensite with retained austenite phases and the (Fe, Cr)23 C6 carbides were identified within the overlay coatings. The presence of the carbon and chromium elements in hard surfaced specimens (as denoted by 307 and 420) produced by single and double pass were increased. The wear resistance in the coatings of 307 and 420 produced by double pass are higher than the coatings produced by single pass. In addition, the amount of average hardness in the coatings of 307 and 420 produced by single and double passes increases from 36 to 38 HRC and from 39 to 42 HRC, respectively. Based on the scanning electron microscopy micrographs, the wear mechanisms of specimens with high hardness are adhesive and tribochemical wear.
منابع مشابه
evaluation of microstructure and wear behavior of iron-based hard - facing coatings on the mo40 steel
mo40 low-alloy steels are mostly used to produce industrial components such as crane wheels whichare exposed to abrasive wear. however, during working conditions, their wear resistance is reduced aftera while due to its low hardness. with increasing abrasive wear, the dimensions of components decreaseand they need to be repaired for surface modification. in this regard, hard overlay coatings ar...
متن کاملhistological evaluation of the effect of three medicaments; trichloracetic acid, formocresol and mineral trioxide aggregate on pulpotomized teeth of dogs
چکیده ندارد.
15 صفحه اولthe effect of functional/notional approach on the proficiency level of efl learners and its evaluation through functional test
in fact, this study focused on the following questions: 1. is there any difference between the effect of functional/notional approach and the structural approaches to language teaching on the proficiency test of efl learners? 2. can a rather innovative language test referred to as "functional test" ge devised so so to measure the proficiency test of efl learners, and thus be as much reliable an...
15 صفحه اولcellular behavior and scanning electron microscope evaluation of pro-root mta, root mta and modified mta on fibroblast l929
چکیده ندارد.
15 صفحه اولEffect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 12 شماره 1
صفحات 1- 8
تاریخ انتشار 2015-09-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023