Enhancing Mechanical Strength of Inorganic Geopolymer by Using Phenol Resin

نویسندگان

Amir Kamalloo Ceramic Department, Materials and Energy Research Center

sadra emami Chemical and materials eng, University of Dayton

چکیده مقاله:

The effect of organic phenol on the compressive and flexural strength of a metakaolin based geopolymer is studied. It was found that 12 wt% phenol resins can increase the compressive and flexural strength by 30% and 65% respectively. In addition, the reinforcing effect of phenol resin is higher in Na-PS and Na-PSS type geopolymers rather than Na-PSDS. Two distinct endothermic peaks were detected in DTA curve which can be attributed to the release of water from phenol resin and its final thermal decomposition.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Factors Influencing Compressive Strength of Geopolymer Concrete

To study effects of several factors on the properties of fly ash based geopolymer concrete on the compressive strength and also the cost comparison with the normal concrete. The test variables were molarities of sodium hydroxide(NaOH) 8M,14M and 16M, ratio of NaOH to sodium silicate (Na2SiO3) 1, 1.5, 2 and 2.5, alkaline liquid to fly ash ratio 0.35 and 0.40 and replacement of water in Na2SiO3 s...

متن کامل

Preparation and Characterization of New Geopolymer-Epoxy Resin Hybrid Mortars

The preparation and characterization of metakaolin-based geopolymer mortars containing an organic epoxy resin are presented here for the first time. The specimens have been prepared by means of an innovative in situ co-reticulation process, in mild conditions, of commercial epoxy based organic resins and geopolymeric slurry. In this way, geopolymer based hybrid mortars characterized by a differ...

متن کامل

Enhancing the low cycle fatigue strength of AA6061 aluminum alloy by using the optimized combination of ECAP and precipitation hardening

In the present study, mechanical properties and low cycle fatigue behavior of a solid-solutionized AA6061 aluminum alloy produced by equal channel angular pressing (ECAP) process were investigated. The grain refinement after two passes of ECAP significantly increased the yield stress and ultimate tensile stress and decreased the ductility of the alloy. However, the improvement of low cycle fati...

متن کامل

Effect of Modification with Phenol Formaldehyde Resin on the Mechanical Properties of Wood from Chinese Fir

Samples of Chinese fir were treated with either low-molecular-weight or commercial phenol-formaldehyde (PF) resins. The macroand micromechanical properties of the treated and untreated samples were determined. The average longitudinal tensile modulus of elasticity (MOE) was 30.88% larger for the samples treated with the low-molecular-weight PF resin than it was for the untreated samples. The av...

متن کامل

Desorption by Ultrasound: Phenol on Activated Carbon and Polymeric Resin

An experimental feasibility study of using ultrasound to accomplish the dificult desorption of phenol from activated carbon and polymeric resin adsorbents is discussed. The desorption rates of activated carbon were found to significantly increase by ultrasound at 40 kHz and 1.44 MHz. Attrition of the activated carbon due to cavitation could be prevented by operating at a higher frequency and wi...

متن کامل