Electrochemical Characterization of a Martensitic Stainless Steel
نویسنده
چکیده مقاله:
This paper focused on the characterization of electrochemical behavior of a martensitic stainless steel in the acidic solutions. For this purpose, electrochemical parameters were derived from potentiodynamic polarization, Mott Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that corrosion current density of AISI 420 stainless steel was decreased with the decrease in the concentration of solution. EIS studies also showed that as concentration was decreased, the measured value of polarization resistance was increased. This trend was due to the decrease in the corrosion current density, which corresponded to potentiodynamic polarization curves. Mott Schottky analysis revealed that passive films behaved as n-type and p-type semiconductors at potentials below and above the flat band potential, respectively. Also, Mott Schottky analysis indicated that the donor and acceptor densities were increased with solution concentration.
منابع مشابه
electrochemical characterization of a martensitic stainless steel
this paper focused on the characterization of electrochemical behavior of a martensitic stainless steel inthe acidic solutions. for this purpose, electrochemical parameters were derived from potentiodynamicpolarization, mott schottky analysis and electrochemical impedance spectroscopy (eis) techniques.the potentiodynamic polarization results showed that corrosion current density of aisi 420 sta...
متن کاملCharacterization of a Laser Surface-Treated Martensitic Stainless Steel
Laser surface treatment was carried out on AISI 416 machinable martensitic stainless steel containing 0.225 wt.% sulfur. Nd:YAG laser with a 2.2-KW continuous wave was used. The aim was to compare the physical and chemical properties achieved by this type of selective surface treatment with those achieved by the conventional treatment. Laser power of different values (700 and 1000 W) with four ...
متن کاملThermoelectric Power Studies on a Martensitic Stainless Steel
In this work the different contributions to the thermoelectric power (TEP) measurement during the dissolution process of M23C6 carbides in an X45Cr13 stainless steel have been evaluated. Thus, the influences of carbon and chromium contents in solid solution in the austenite, the austenite grain boundaries and the microstructure on the TEP have been determined.
متن کاملNanotribological behavior of deep cryogenically treated martensitic stainless steel
Cryogenic treatments are increasingly used to improve the wear resistance of various steel alloys by means of transformation of retained austenite, deformation of virgin martensite and carbide refinement. In this work the nanotribological behavior and mechanical properties at the nano-scale of cryogenically and conventionally treated AISI 420 martensitic stainless steel were evaluated. Conventi...
متن کاملElectrochemical deprotonation of phosphate on stainless steel
Voltammetric experiments performed in phosphate buffer at constant pH 8.0 on platinum and stainless steel revealed clear reduction currents, which were correlated to the concentrations of phosphate. On the basis of the reactions proposed previously, a model was elaborated, assuming that both H2PO4 and HPO4 2 underwent cathodic deprotonation, and including the acid–base equilibriums. A kinetic m...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 10 شماره 2
صفحات 1- 6
تاریخ انتشار 2013-12-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023