Electrochemical and Tribological Behaviour of Oxide Dispersion Strengthened Duplex Stainless Steel in Mine Water Environment

electrochemical and tribological behaviour of oxide dispersion strengthened duplex stainless steel in mine water environment

abstract this work investigated the electrochemical and aqueous tribological behavior of hot pressed 2205 duplex stainless steel (dss). dss sintered composites of different volume percent (% vol) of partially stabilized zirconia (psz) was developed using powder metallurgy (pm) technique. electrochemical behaviour was studied at room temperature, using open circuit potential and potentiodynamic ...

Surface Texturing-Plasma Nitriding Duplex Treatment for Improving Tribological Performance of AISI 316 Stainless Steel

Surface texturing-plasma nitriding duplex treatment was conducted on AISI 316 stainless steel to improve its tribological performance. Tribological behaviors of ground 316 substrates, plasma-nitrided 316 (PN-316), surface-textured 316 (ST-316), and duplex-treated 316 (DT-316) in air and under grease lubrication were investigated using a pin-on-disc rotary tribometer against counterparts of high...

ELECTROCHEMICAL BEHAVIOUR OF AISI 304 STAINLESS STEEL IN SULFURIC SOLUTION: EFFECTS OF ACID CONCENTRATION

The effects of H2SO4 concentration on the electrochemical behaviour of passive films formed on AISI 304 stainless steel were investigated using by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Potentiodynamic polarization indicated that the corrosion potentials were found to shift towards negative direction with an increase in solution co...

Microstructure, Mechanical and Tribological Properties of Oxide Dispersion Strengthened High-Entropy Alloys

A novel metal matrix composite CrMnFeCoNi with Y₂O₃ as reinforcement phase was designed and manufactured by mechanical alloying and spark plasma sintering. After sintering at 900 °C for 5 min, the microstructure consisted of a FCC matrix and Y₂O₃ nanoparticles. The addition of 0.25 wt % Y₂O₃ increased the room temperature tensile strength of the CrMnFeCoNi base from 868 MPa to 1001 MPa, while t...

Corrosion Performance and Tribological Properties of Carbonitrided 304 Stainless Steel

Water Lubrication of Stainless Steel using Reduced Graphene Oxide Coating

Lubrication of mechanical systems using water instead of conventional oil lubricants is extremely attractive from the view of resource conservation and environmental protection. However, insufficient film thickness of water due to low viscosity and chemical reaction of water with metallic materials have been a great obstacle in utilization of water as an effective lubricant. Herein, the frictio...