Effect of Harmonic Vibration on Microstructure and Mechanical Properties of AA-5083-H321 Aluminum Alloy GMAW Welds
نویسندگان
چکیده مقاله:
In this research, the effect of vibration at the resonant range (75 Hz) on the hardness and tensile strength of AA-5083-H321 aluminum alloy, were welded by gas metal arc welding (GMAW) investigated. Vibration forces were ranged from 850 N to 2200 N, under identical welding parameters. Tensile strength and hardness testing of welded samples were performed. After mechanical tests, the fracture surfaces of welds were examined using scanning electron microscope (SEM) and discussed. The results showed that with increasing vibration force, the tensile strength and fracture strength of the specimens were welded during vibration, were increased by about 3 and 9 percent, respectively, compared to the non-vibrated weld sample. However, no significant change was observed in the hardness of the welded specimens. Mean grains size and heat affected zone of the sample was welded was welded with conventional GMAW, were about 200 μm and 1800 μm, but due to inducing vibration, as vibration force increased from 850 N to N 2200 N, Mean grains size was reduced to about 75 μm and HAZ was reduced from about 1000 μm to 700 μm, that is, about 44 to 61%.
منابع مشابه
determination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولMicrostructure and mechanical properties of friction spot welds of dissimilar AA 5754
In the present study, friction spot welding or refill friction stir spot welding was performed to consolidate dissimilar AA5754 Al and AZ31 Mg alloys. The intermetallic compounds of Al12Mg17 and Al3Mg2 were primarily found in the weld, distributed at the interface between the base materials and in the Al top sheet. The distribution of the intermetallic compounds and the interfacial area between...
متن کاملEffect of Aluminum on the Microstructure and Mechanical Properties of Austempered Ductile Iron Alloys
متن کامل
Effect of Aluminum on the Microstructure and Mechanical Properties of Austempered Ductile Iron Alloys
متن کامل
Microstructure and Mechanical Properties of an Ultrasonic Spot Welded Aluminum Alloy: The Effect of Welding Energy
The aim of this study is to evaluate the microstructures, tensile lap shear strength, and fatigue resistance of 6022-T43 aluminum alloy joints welded via a solid-state welding technique-ultrasonic spot welding (USW)-at different energy levels. An ultra-fine necklace-like equiaxed grain structure is observed along the weld line due to the occurrence of dynamic crystallization, with smaller grain...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 5 شماره 1
صفحات 137- 149
تاریخ انتشار 2019-09
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023