Dealloying and Stress Corrosion Craking of Copper Alloys in Cu(I) Solutions

Study of Copper Bearing Alloys Corrosion Characteristics

This paper addresses investigation of the corrosion behavior of copper bearing anodes with high nickel content. Anodes are produced from different solid wastes formed during the copper or nickel row materials treatment. Nickel content in anode samples had values up to 10 mas %. The content of tin, lead and antimony was up to 1 % for each of elements. Sulphuric acid solution, concentration of 17...

Tarnish Resistance, Corrosion and Stress Corrosion Cracking of Gold Alloys

Tarnishing, corrosion and stress corrosion cracking (SeC) of gold alloys are related phenomena. They present problems when they occur in gold jewellery, dental gold alloys and electronic devices. They are exploited, however, in the depletion gilding and finishing of gold jewellery; and in the extraction, refining and fire assaying of gold. There is still much that is not known about these pheno...

Corrosion Mechanism of Al-zn-in Alloys in Chloride Solutions

The electrochemical behavior of Al-ZnIn alloys was investigated in chloride media by means of potentiodynamic techniques, complemented by Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Analysis (EDX) and Transmission Electron Microscopy (TEM). The influence of local alkalization produced by previous cathodization was analyzed at potentials more negative than the rest potential. The...

Corrosion Protection of Magnesium Alloys in Industrial Solutions

Polystyrene films as barrier layers for corrosion protection of copper and copper alloys.

Dip-coated polystyrene layers of sub-micrometre thickness (85-500nm) have been applied on copper and copper alloys (aluminium brass, copper-nickel 70/30), as well as on stainless steel 304, and produced an effective barrier against corrosion and adhesion of corrosion-relevant microorganisms. According to the dynamic wettability measurements, the coatings exhibited high advancing (103°), recedin...

Corrosion Performance of Copper - Diamond Composites in Different Aqueous Solutions

In the present work copper/diamond composites, such as (Cu-10 Vf % diamond uncoated, Cu-30 Vf % diamond uncoated, Cu-10 Vf % diamond coated NiCrB and Cu-30 Vf % coated NiCrB) as heat sink materials have been fabricated using powder metallurgy and electroless techniques. The copper powder used in this study has been fabricated using electroless technique and the diamond powder was electroless co...