Characterization of CaSn(OH)6 and CaSnO3 Nanostructures Synthesized by a New Precursor

نویسندگان

  • D. Ghanbari Young Researchers and Elite Club, Arak Branch, Islamic Azad University, Arak, Iran
  • M. Salavati-Niasari Institute of Nano Science and Nano Technology, University of Kashan, Kashan, P.O. Box, 87317-51167, I. R. Iran.
  • S. Moshtaghi Institute of Nano Science and Nano Technology, University of Kashan, Kashan, P.O. Box, 87317-51167, I. R. Iran.
چکیده مقاله:

In this paper, calcium stannate nanoparticles were synthesized by a fast and simple co-precipitation procedure. For CaSnO3 preparation ammonia was used as precipitation agent. The effect of various surfactants such as cationic, anionic and neutral on the morphology of the products was investigated. By changing in Ca(Sal)2 as a new precursor different morphologies were obtained. Ligand as a capping agent with steric hindrance leads to preparation of product with lower particle size. These semiconductor nanostructures have photo-catalyst activities and can degrade organic dyes as water pollution. The synthesized materials were characterized by X-ray diffraction (XRD) technique, scanning electron microscopy (SEM) Fourier transform infrared (FT-IR) and UV-visible spectroscopy.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

characterization of casn(oh)6 and casno3 nanostructures synthesized by a new precursor

in this paper, calcium stannate nanoparticles were synthesized by a fast and simple co-precipitation procedure. for casno3 preparation ammonia was used as precipitation agent. the effect of various surfactants such as cationic, anionic and neutral on the morphology of the products was investigated. by changing in ca(sal)2 as a new precursor different morphologies were obtained. ligand as a capp...

متن کامل

Synthesis and characterization of high-temperature ceramic YBCO nanostructures prepared from a novel precursor

As a new precursor, [tris(2-hydroxyacetophenato) triaqua(III)], [Y(HAP)3(H2O)3]; complex was used in thermal decomposition process for the synthesis of rod-like high-temperature ceramic YBCO with length of about 320-350 nm and diameters 60–90 nm. The as-synthesized products were characterized by XRD, FT-IR, TEM, SEM and EDX analyses. The results showed that by u...

متن کامل

Synthesis, Characterization and Catalytic Activity of CuO Nanostructures using Schiff Base Copper Complexes as a Precursor

Two Cu(II) complexes, [Cu(L1)2](NO3)2 (1) and [Cu(L2)2] (NO3)2(2), which L1 and L2 Schiff base ligands are 2-(thiophene-2-yl) -1H-imidazo [4,5-f] [1,10] phenanthroline and 2-(furane-2-yl)-1H-imidazo[4,5-f] [1,10] phenenthroline, respectively, were syn...

متن کامل

synthesis and characterization of some new cyclometalated organoplatinum(ii) complexes containing phosphite ligand

در این تحقیق روشی جهت سنتز یک سری از کمپلکس های پلاتین (ii) حاوی لیگاند های دهنده ی فسفری شامل فسفیت و فسفین ارائه شده است. واکنش پیش ماده ی پلاتین (ii)،trans/cis- [ptcl2(sme2)2] ، با 2 اکی مولار از لیگاند p(oph)3در حلال بنزن کمپلکس1، cis-[ptcl2(p(oph)3)2] را تولید می نماید. جهت سنتز کمپلکس سایکلو متال فسفیتی، کمپلکس 1 با 1 اکی والان واکنشگر ptcl2 در حلال زایلن در شرایط رفلاکس زیر گاز آرگون م...

solution of security constrained unit commitment problem by a new multi-objective optimization method

چکیده-پخش بار بهینه به عنوان یکی از ابزار زیر بنایی برای تحلیل سیستم های قدرت پیچیده ،برای مدت طولانی مورد بررسی قرار گرفته است.پخش بار بهینه توابع هدف یک سیستم قدرت از جمله تابع هزینه سوخت ،آلودگی ،تلفات را بهینه می کند،و هم زمان قیود سیستم قدرت را نیز برآورده می کند.در کلی ترین حالتopf یک مساله بهینه سازی غیر خطی ،غیر محدب،مقیاس بزرگ،و ایستا می باشد که می تواند شامل متغیرهای کنترلی پیوسته و گ...

synthesis and characterization of high-temperature ceramic ybco nanostructures prepared from a novel precursor

as a new precursor, [tris(2-hydroxyacetophenato) triaqua(iii)], [y(hap)3(h2o)3]; complex was used in thermal decomposition process for the synthesis of rod-like high-temperature ceramic ybco with length of about 320-350 nm and diameters 60–90 nm. the as-synthesized products were characterized by xrd, ft-ir, tem, sem and edx analyses. the results showed that by using fine raw materials, the calc...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 5  شماره 2

صفحات  169- 174

تاریخ انتشار 2015-04-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023