Catalytic Performance and Characterization of Promoted K-La/ZSM-5 Nanocatalyst for Biodiesel Production

نویسندگان

  • Fataneh Jafari Department of Physical Chemistry, Faculty of Chemistry, Razi University, P. O. Box 6714967346 Kermanshah, I.R. IRAN
  • Mostafa Feyzi Department of Physical Chemistry, Faculty of Chemistry, Razi University, P. O. Box 6714967346 Kermanshah, I.R. IRAN
  • Parasto Nouri Department of Applied Chemistry, Faculty of Chemistry, Razi University, Kermanshah, I.R. IRAN
چکیده مقاله:

The promoted K-La nanocatalysts supported on ZSM-5 zeolite were prepared via wetness impregnation method and tested for biodiesel production from soybean oil. The effects of different weight percentage of La, loading of K as a promoter and calcination conditions on structure and activity of catalyst were investigated. Results showed that the supported catalyst containing 7wt.% of La was promoted with 1wt.% of K is an optimal catalyst for biodiesel production. The best operational conditions were the CH3OH/oil=12/1 molar ratio at 60˚C with mechanical stirring 500 rpm for 3 h. The biodiesel yield reached 90% under the optimal operational conditions. It was found that K-La/ZSM-5 nanocatalyst have high basic sites and catalytic activity for biodiesel production. Characterization of catalysts was carried out by using Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), Temperature Programmed Desorption (TPD), X-Ray Diffraction (XRD), Fourier Transform-InfraRed(FT-IR) spectroscopy and N2 adsorption-desorption measurements methods.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Normal Heptane Reforming of Promoted Platinum Composite Catalysts: Preparation, Characterization and Catalytic Performance

Pt/Zr(x)-HMS/HZSM-5 catalysts with different ratios of Silicium/Zirconium (denoted as x) were studied for normal heptane reforming at 350-450 °C temperature range. For this purpose, the properties of the catalysts such as X-ray diffraction, X-ray fluorescence, Fourier-transform infrared spectroscopy, Ultraviolet–visible diffuse reflectance spectroscopy, NH3-temperature pro...

متن کامل

KCl Promoted Cobalt-iron Nanocatalysts Supported on Silica: Catalytic Performance and Characterization in Fischer-Tropsch Synthesis

The SiO2 supported cobalt-iron nano catalysts were prepared by the sol-gel method. This research investigated the effects of (Co/Fe) wt.%, different Co/Fe ratio at different temperature and loading of KCl wt.% for Fisher-Tropsch synthesis (FTS). The results were showed that the catalyst containing 50 wt.% (Co/Fe)/SiO2 (Co/Fe ratio is 70/30) which promoted with 0.6 wt.% KCl is an optimal nano ca...

متن کامل

performance of biological system and advanced oxidation processes (aop) treating antibiotic production industrial wastewater

در این مطالعه، عملکرد دو سیستم اکسیداسیون شیمیایی پیشرفته و یک سیستم بیولوژیکی برای حذف آموکسی سیلین در فاضلاب های سنتزیدر غلظت های مشابه با موارد صنعتی مورد بررسی قرار گرفته شدند. مطالعه انجام شده دارای سه بخش متفاوت اکسیداسیون با ازن و اشعه uv، اکسیداسیون با استفاده از نانو فتوکاتالیست tio2 و استفاده از بیوراکتور هوازی لجن فعال با جداکننده های فیزیکی می باشد. در هر بخش، متغیر های متفاوتی متنا...

15 صفحه اول

Catalytic Behaviour of MnZrOx System for Heterogenous Biodiesel Production

Manganese/zirconium mixed oxides catalysts (MnZrOx), characterized by high Mn loading (up to 50%), along with high specific surface area, have been investigated in the transesterification reaction of sunflower oil. Catalysts were found to be very active by operating at low catalyst/oil ratio (1 wt.%). The high activity was justified on the basis of both the marked basic character of such system...

متن کامل

High performance catalytic distillation using CNTs-based holistic catalyst for production of high quality biodiesel

For production of biodiesel from bio oils by heterogeneous catalysis, high performance catalysts of transesterification and the further utilization of glycerol have been the two points of research. The process seemed easy, however, has never been well established. Here we report a novel design of catalytic distillation using hierachically integrated CNTs-based holistic catalyst to figure out th...

متن کامل

Kinetic Study on the CsXH3−X PW12O40/Fe-SiO2 Nanocatalyst for Biodiesel Production

The kinetic of the transesterification reaction over the Cs(x)H(₃-x)PW₁₂O₄₀/Fe-SiO₂ catalyst prepared using sol-gel and impregnation procedures was investigated in different operational conditions. Experimental conditions were varied as follows: reaction temperature 323-333 K, methanol/oil molar ratio = 12/1, and the reaction time 0-240 min. The H₃PW₁₂O₄₀ heteropolyacid has recently attracted s...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 37  شماره 2

صفحات  33- 44

تاریخ انتشار 2018-04-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023