An Experimental Investigation on Fracture Analysis of Polymer Matrix Composite under Different Thermal Cycling Conditions
نویسندگان
چکیده مقاله:
Fracture analysis of glass/epoxy composites under different thermal cycling conditions is considered. Temperature difference, stacking sequence, fiber volume fraction and number of thermal cycles are selected as the experimental design factors. The Taguchi method is implemented to design of the experiment and an apparatus is developed for automatic thermal cycling tests. The tensile tests are done to study mechanical behavior of the specimens after the thermal cycling. The results show that the stacking sequence is the main effective factor on the fracture surface behavior of the specimens. Also, long splitting, lateral and angled breakage are the dominate failure mode of [0]8, [02/902]s and [0/±45/90]s layups, respectively. It’s found that the thermal cycling and temperature difference cause to increase the surface matrix loss significantly. This surface matrix loss can be an initial region to matrix debonding and crack propagation. Also, when the angle difference between lamina is increased the mechanical properties are reduced under the thermal cycling, significantly.
منابع مشابه
Surface Degradation of Polymer Matrix Composites Under Different Low Thermal Cycling Conditions
The principal effects of mass degradation on polymer matrix composites (PMCs) are the decay of mechanical properties such as strength, elongation, and resilience. This degradation is a common problem of the PMCs under thermal cycling conditions. In this article, composite degradation was investigated by measurement of total mass loss (TML) using the Taguchi approach. Thermal cycling tests were ...
متن کاملsurface degradation of polymer matrix composites under different low thermal cycling conditions
the principal effects of mass degradation on polymer matrix composites (pmcs) are the decay of mechanical properties such as strength, elongation, and resilience. this degradation is a common problem of the pmcs under thermal cycling conditions. in this article, composite degradation was investigated by measurement of total mass loss (tml) using the taguchi approach. thermal cycling tests were ...
متن کاملinvestigation of effective parameters on the rigidity of light composite diaphragms (psscb) by fem
در این رساله با معرفی سقف های psscb متشکل از ترکیب ورق های فولادی ذوزنقه ای و تخته های سیمانی الیافی به عنوان سقف های پیش ساخته (سازگار با سیستم سازه ای قاب های فولادی سبک) به بررسی پارامترهای موثر بر صلبیت سقف، پرداخته می شود. در تحقیق حاضر ابتدا به مدل سازی دو نمونه سقف آزمایش شده، به روش اجزاء محدود با استفاده از نرم افزار تحلیلی abaqus ver 6.10 پرداخته شده است. نمونه های ساخته شده تحت اعما...
Open-Hole Size and Thermal Cycling Effects on Mass Loss and Surface Degradation of Polymer Matrix Composites
Degradation is a common problem for polymer matrix composites (PMCs) under low thermal cycling conditions. This paper investigates the effects of low thermal cycling on total mass loss (TML) and surface degradation of PMCs. Unnotched and open-hole specimens were weighed before and after low thermal cycling. The total mass loss and surface degradation of the specimens were studied over 250 cycle...
متن کاملInvestigation of the Synthesis of Chitosan Coated Iron Oxide Nanoparticles under Different Experimental Conditions
Iron oxide (Fe3O4) nanoparticles with average sizes of 10 nm were synthesized by a chemical coprecipitation method in the presence of chitosan. Chitosan as a natural polymer which can be extracted from crustaceans was used in the synthesis process in order to achieve more dispersed nanoparticles. Also, chitosan was used to obtain functionalized magnetic nanoparticles for using in different area...
متن کاملINVESTIGATION ON THERMAL PROPERTIES OF Al/SiCp METAL MATRIX COMPOSITE BASED ON FEM ANALYSIS
Computational simulations on the thermal analysis of metal matrix composite (MMC) composed of Al and SiC were performed in extended areas of SiC volume fraction. Due to the experimental limitations, only the narrow range of SiC volume fraction has been examined. Through the simulation, which enables current experimental situation to extend, we attempted to explore the dependencies of thermal an...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 9 شماره 4
صفحات 697- 706
تاریخ انتشار 2017-12-30
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023