A study on the sub-structure and mechanical properties of friction stir processed AA 6061-T6 joints with ultra-fine grained structure

نویسندگان

  • Ali Salemi Golezani Department of Materials Engineering, Karaj Branch, Islamic Azad University, Karaj, Iran.
  • M. Esmaily Department of Chemical and Biological Engineering, Chalmers University of Technology, Göteborg, Sweden.
  • N. Mortazavi Department of Applied Physics, Chalmers University of Technology, Göteborg, Sweden.
چکیده مقاله:

Ultra-fine grained (UFG) structure (~0.6 µm) was produced in the stir zone (SZ) of 6061-T6 aluminum alloy joints using friction stir processing (FSP) cooled by liquid nitrogen (N2). A new experimental set-up was used to simultaneously quench the lower and upper surfaces of the samples during the processing. In addition, FSPed joints, using a steel backing plate, were produced at room temperature as a reference. Sub-structural studies have been carried out to investigate the occurrence of dynamic recrystallization and grain growth in the weld area of the samples. The results indicate that the microstructure was not fully recrystallized as a high dislocation density (3.5×1014 m-2) was measured in the stir zone (SZ) of rapidly cooled joints in compare with that of the air-cooled joints (1.5×1014 m-2). Moreover, the rapid cooling generated a very high dislocation density of about 6.5×1014 m-2 in the thermo-mechanical affected zone (TMAZ). Accordingly, better mechanical properties were obtained in the SZ. In contrast, lower strain hardening capacity and hardening exponent values were obtained in the rapidly cooled joints where the highest fraction of low angle grain boundaries (LAGBs) and largest number of dislocations were measured.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Microstructure and Mechanical Properties of Dissimilar Friction Stir Welding between Ultrafine Grained 1050 and 6061-T6 Aluminum Alloys

The ultrafine grained (UFGed) 1050 Al plates with a thickness of 2 mm, which were produced by the accumulative roll bonding technique after five cycles, were friction stir butt welded to 2 mm thick 6061-T6 Al alloy plates at a different revolutionary pitch that varied from 0.5 to 1.25 mm/rev. In the stir zone, the initial nano-sized lamellar structure of the UFGed 1050 Al alloy plate transforme...

متن کامل

Feasibility study of friction stir welding of 6061-T6 aluminium alloy with AISI 1018 steel

The present work demonstrates that friction stir welding (FSW) is a feasible route for joining 6061 aluminium (Al) alloy to AISI 1018 steel. The weld has a good weld quality and is free of cracks and porosity. The tensile failure happened at the boundary between the nugget and thermomechanically affected zone of the base Al alloy, indicating that the weld has a higher joining strength. Despite ...

متن کامل

Effect of heat treatment on the grain structure and mechanical properties of Al-7075 friction stir weld

The fine grain structure of friction-stir welded aluminum alloys is unstable during post weld heat treatment and some grains abnormally grown. In this study, the sequence of abnormal grain growth during T6 heat treatment of Al-7075 friction-stir weld and its effect on mechanical properties of the weld was studied. The results showed that heat treatment in 510 ˚C resulted in drastic grain growth...

متن کامل

Effect of Heat Input on Tensile Properties of Friction Stir Welded AA6061-T6 and AA7075-T6 Dissimilar Aluminum Alloy Joints

Friction Stir Welding (FSW) is a solid state process widely used to join dissimilar aluminium alloys. High quality and strength joints can be fabricated using this technique when compared to other conventional methods. The welding parameters play major role in determining the quality of the weld. This paper aims in presenting the effect of heat input on tensile properties of the joints between ...

متن کامل

Effect of heat treatment on the grain structure and mechanical properties of Al-7075 friction stir weld

The fine grain structure of friction-stir welded aluminum alloys is unstable during post weld heat treatment and some grains abnormally grown. In this study, the sequence of abnormal grain growth during T6 heat treatment of Al-7075 friction-stir weld and its effect on mechanical properties of the weld was studied. The results showed that heat treatment in 510 ˚C resulted in drastic grain growth...

متن کامل

the underlying structure of language proficiency and the proficiency level

هدف از انجام این تخقیق بررسی رابطه احتمالی بین سطح مهارت زبان خارجی (foreign language proficiency) و ساختار مهارت زبان خارجی بود. تعداد 314 زبان آموز مونث و مذکر که عمدتا دانشجویان رشته های زبان انگلیسی در سطوح کارشناسی و کارشناسی ارشد بودند در این تحقیق شرکت کردند. از لحاظ سطح مهارت زبان خارجی شرکت کنندگان بسیار با هم متفاوت بودند، (75 نفر سطح پیشرفته، 113 نفر سطح متوسط، 126 سطح مقدماتی). کلا ...

15 صفحه اول

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 2  شماره 1

صفحات  33- 46

تاریخ انتشار 2014-02-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023