مقایسه استحکام باند سمان رزینی با کامپوزیت غیر مستقیم آماده شده با توان‌های لیزر ER YAG و سندبلاست

  Background and Aims: Indirect composites are designed to overcome the shortcomings of direct composites such as polymerization shrinkage and low degree of conversion. But, good adhesion of resin cements to indirect composites is still difficult. This research was designed to assess the effect of different powers of ErYAG laser compared with sandblasting. On the micro tensil bond strength of resin cement to indirect composites.   Materials and Methods: Specimens were prepred using dental resin composite (Gradia GC) and metallic mold (15×5×5 mm) and were cured according to the manufacturer’s instructions. 24 blocks were prepared and randomly divided into 12 groups. G1:no treatment (as control), G 2-6: Er YAG laser irradiation (2, 3, 4, 5, 6 Watt), G7: sandblast. Two composite blocks were bonded to each other with Panavia F.2. resin cement. The cylindrical sections with dimensions of 1 mm were tested in a microtensile bond strength tester device using 0.5 mm/min speed until fracture points. Data were analyzed using 2-way ANOVA and T-test.   Results: Interaction between lasers irradiation and sandblast treatments were significant (P0.05) whether samples were sandblasted or not. Samples which received 300 mJ of laser showed lower bond strength compared with no laser treatment. Other groups showed no significant difference (P>0.05).   Conclusion: It seems that application of sandblast with proper variables, is a good way to improve bond strength.Laser application had no influence in improving the bond strength between the indirect composite and resin cement.