مشخصه یابی و مکانیزم تشکیل نانوکامپوزیت زمینه آلومینیمی تقویت شده با ذرات TiO2 به روش آسیاب مکانیکی
نویسندگان
چکیده مقاله:
In the present study, pure Aluminum powder with 5%wt Titanium Dioxide was mechanically milled at different times. Using phase analysis through X-ray diffraction (XRD), it was found that increasing of the milling times over 10 hours causes the reduction of Titanium by Aluminum and formation of Al2O3 in the structure. Also, it was shown that if the process persists, Aluminum reacts with Titanium and causes the formation of Al3Ti in the composition. The reactions were studied through the thermodynamic relations. Furthermore, after distribution of reinforcement particles in the matrix, using X-ray diffraction peak broadening, according to Williamson-Hall equation, the mean crystallite size and lattice strain were determined, and by scanning electron microscopy (SEM), the structure and morphology of the powder particles were studied.
منابع مشابه
مشخصه یابی و مکانیزم تشکیل نانوکامپوزیت زمینه آلومینیمی تقویت شده با ذرات tio۲ به روش آسیاب مکانیکی
در پژوهش حاضر پودر آلومینیوم خالص به همراه 5 درصد وزنی دی اکسید تیتانیم، در زمان های مختلف تحت فرایندآسیاب کاری مکانیکی قرار گرفتند. با استفاده از تحلیل فازی به وسیله پراش پرتو ایکس(xrd) مشخص شد که افزایش زمان آسیاب به بیش از 10 ساعت سبب احیای تیتانیم توسط آلومینیوم شده و al2o3 در ساختار تشکیل می شود. با ادامه فرایند، آلومینیوم با تیتانیم واکنش می دهد و سبب تشکیل al3ti در ترکیب می شود. این واکن...
متن کاملمشخصه یابی ساختاری پودر نانوکامپوزیت زمینه پلیمری PTFE/Al2O3 تولید شده به روش آسیاب کاری گلوله ای پرانرژی
متن کامل
تولید، مشخصه یابی و ارزیابی خواص مکانیکی نانوکامپوزیت آلیاژ پایه کبالت با تقویت کننده نانوپودر فورستریت
Short life of current total hip replacement metallic implants is generally dependent on the aseptic loosening of the implant, which occurs due to mismatch of elastic modulus between bone and metallic implant materials. Decreasing in elasticmodulus of implant could be successful. Forsterite is biocompatible and bioactive ceramic which has suitable mechanical properties. In presented research the...
متن کاملمشخصه یابی ساختاری پودر نانوکامپوزیت زمینه پلیمری ptfe/al2o3 تولید شده به روش آسیاب کاری گلوله ای پرانرژی
متن کامل
تولید و مشخصه یابی کامپوزیت نانوساختار Al-Mg-Zn/ 3 wt.% Al2O3 بوسیله زمینه پیش آسیاب شده توسط آلیاژسازی مکانیکی
Al-Zn-Mg/3 wt-% Al2O3 nanostructured composite powder was synthesized through Mechanical Alloying (MA). At first, the 7014 alloy matrix constituents were milled in a planetary ball mill for 20 hours. Then, 3 wt.% µ-Al2O3 particles were added to the pre-milled matrix and the nanostructured composite powder was produced at different MA times to investigate the effects of MA time ...
متن کاملمدل سازی آماری فرایند تولید ذرات نانوکامپوزیت پایه آلومینیم تقویت شده با ذرات SiC به روش آلیاژسازی مکانیکی
در تحقیق حاضر فرایند آلیاژسازی مکانیکی جهت تولید پودر نانوکامپوزیت پایه آلومینیم تقویت شده توسط ذرات نانومتری SiC به روش‌های آماری مدل‌سازی شده است. در ابتدا، از میان عوامل متعدد، عوامل موثرتر جهت تحلیل فرایند برگزیده شد‌ه‌اند. سپس آزمایش‌های عملی جهت تهیه پودر نانوکامپوزیت برنامه‌ریزی و انجام شده است. با توجه به این که آلیاژسازی مکانیکی متأثر از پارامترهای متعدد و پیچیده‌ای است، مدل‌سازی ک...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 33 شماره 2
صفحات 99- 106
تاریخ انتشار 2015-03
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023