In recent years, much research in the field of advanced materials synthesis using the mechanochemical process has been performed. In this study, Al2O3-TiN nanocomposite was produced by the mechanochemical method and using inexpensive material TiO2 (instead of pure titanium which is too expensive). Also, aluminum and titanium oxide powders were used as raw materials. Milling under N2 atmosphere with 5 atmospheric pressure was performed and the products were evaluated by the SEM and XRD. Milling results showed that in the first stage of the synthesis process, titanium oxide is reduced by aluminum and the process continues, producing titanium reaction with nitrogen. When the Al/TiO2 ratio molar is equal to 1.2 and 1.3, after 20 hours of milling, TiN peaks in the XRD appears. Moreover, the results showed that milling leads to the formation of fine and spherical particles.
منابع مشابه
سنتز پودر نانوکامپوزیت al۲o۳-tin توسط مکانوشیمیایی
درسالهای اخیر، تحقیقات زیادی در زمینه استفاده از فرایند مکانوشیمیایی برای سنتز مواد پیشرفته صورت گرفته است. در این تحقیق، نانوکامپوزیت al2o3-tin به روش مکانوشیمیایی و با استفاده از ماده ارزان قیمت tio2 (به جای تیتانیوم خالص که خیلی گران است) تولید شد. از پودرهای اکسید تیتانیوم و آلومینیوم به عنوان مواد اولیه استفاده شد. آسیابکاری در آتمسفر نیتروژن با فشار 5 آتمسفر انجام شد و محصولات به دست آمده...
متن کاملسنتز نانوکامپوزیت al2o3/mo از اکسید مولیبدن به روش مکانوشیمیایی
مواد نانو کامپوزیت به خاطر ریز دانه بودن و وجود فصل مشترک فوق العاده زیاد، دارای کسر زیادی از اتم ها در مرزدانه ها بوده، به طوری که خواص قابل توجهی را در مقایسه با سایر مواد از خود بروز می دهند. فرآیند های مختلفی همچون ذوب و ریخته گری و یا انجماد سریع و فرآیندهای مکانوشیمیایی برای تولید نانوکامپوزیت ها وجود دارند. قابلیت های منحصر به فرد روش مکانوشیمیایی مانند؛ انجام واکنش ها در حالت جامد، تهیه...
15 صفحه اولاثر زمان آسیابکاری بر تولید نانوکامپوزیت زمینه سرامیکی TixAly/Al2O3 به روش مکانوشیمیایی
In recent years, much research has been performed in the field of nanomaterials synthesis using mechanochemical process. In this research, TixAly/Al2O3 ceramic matrix nanocomposite was produced by the mechanochemical method. Aluminum and inexpensive titanium oxide powders were used as raw materials, and milling was performed under N2 atmosphere. The results showed that reduction of TiO2 by Al i...
متن کاملبررسی تأثیر سرعت آسیاکاری بر تولید نانوکامپوزیت درجای Al2O3-ZrB2 با استفاده از روش مکانوشیمیایی
در این پژوهش اثر سرعت آسیاکاری بر سامانه احتراقی Al/ZrO2/H3BO3مورد بررسی قرار گرفت. بدین منظور پودرهای خام اولیه با نسبتهای استوکیومتری مشخص و نسبت گلوله به پودر 1:10 با سرعتهای350، 450 و500 دور بر دقیقه به مدت 15 ساعت تحت عملیات آسیاکاری قرار گرفتند. همچنین، آنالیز حرارتی افتراقی(DSC ) با نرخ گرمایش°C/min 40 بر روی نمونهها انجام شد. بمنظور بررسی فازهای تشکیل شده، آنالیز فازی XRD بر روی...
متن کاملساخت نانوکامپوزیت پایه سرامیکی al2o3-zrb2 به دو روش سنتز مکانوشیمیایی و سنتز دمای بالای خودپیشرونده
در این پژوهش امکان ساخت کامپوزیت سرامیکی al2o3-zrb2 به دو روش سنتز احتراقی و سنتز مکانوشیمیایی مورد بررسی قرار گرفت. به منظور افزایش تمایل واکنش دهنده ها به سنتز احتراقی، پودرها قبل از فرآیند سنتز، به وسیله آسیا، تحت عملیات فعال سازی مکانیکی قرار گرفتند. با استفاده از آنالیز حرارتی افتراقی اثر سرعت و زمان آسیاکاری بر دمای شروع احتراق و همچنین شدت واکنش ها در مخلوط پودری بررسی شد. نتایج آنالیز ح...
منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 30 شماره 2
صفحات 13- 22
تاریخ انتشار 2011-12
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023