ساخت و بررسی خواص مغناطیسی فریت کبالت به‌روش شیشه سرامیک در سیستم Na2O-Fe2O3-CoO-B2O3-SiO2
نویسندگان
چکیده مقاله:
In this investigation, the effect of heat treatment on magnetic properties of glass and nano-structured cobalt-ferrite glass-ceramic was studied. The glass was synthesized in the system of Na2O-Fe2O3-CoO-B2O3-SiO2. Based on DTA results, heat treatment was done at different times and temperatures. X-ray diffraction pattern of glass-ceramic showed the crystallization of CoFe2O4 and some nonmagnetic phases. The highest magnetization of 11.8 emu/g was obtained for the sample heat-treated for 2 hr at 670C in graphite bed. Average crystallite size of CoFe2O4 in this sample was 50 nm. Scanning Electron Microscopy (SEM) confirmed the formation of cobalt ferrite nanoparticles in the glass matrix.
منابع مشابه
ساخت و بررسی خواص مغناطیسی فریت کبالت به روش شیشه سرامیک در سیستم na۲o-fe۲o۳-coo-b۲o۳-sio۲
در این پژوهش رفتار غیربلورینه شدن ترکیب و تاثیر عملیات حرارتی بر ریزساختار و خواص مغناطیسی شیشه سرامیک سیستم na2o-fe2o3-coo-b2o3-sio2 برای دست یابی به فریت کبالت از روش شیشه-سرامیک مورد بررسی قرار گرفت. شیشه اولیه توسط عبور مذاب از غلطک های فولادی در حال چرخش با سرعت 240 دور بر دقیقه،به دست آمد. نتایج xrd شیشه حاصله دست یابی به یک ماده غیربلورینه را تایید کرد. در ادامه، تحلیل گرمایی در اتمسفر ن...
متن کاملخواص اپتیکی شیشه و شیشه سرامیک نانوساختار SiO2-Na2O-CaO-CaF2 آلاییده با Cr2O3
در این پژوهش اثر یون آلاینده Cr2O3بر خواص اپتیکی، حرارتی و ساختاری شیشه با ترکیب 53%SiO2-17Na2O-17CaO-13CaF2مورد مطالعه قرار گرفته است. هم‌چنین با انجام عملیات حرارتی دو مرحله‌ای در دمای جوانه‌زنی و رشد فاز بلورین نانومتر در شیشه بدون آلاینده و آلاییده شده باCr2O3متبلور گردید. حضور بلورهای نانومتری منجر به تغییر خواص اپتیکی شیشه، کاهش انرژی نوار ممنوعه و انرژی Urbachدر شیشه‌ها شده است. نوع فاز...
متن کاملStructural Investigation of Na2O–B2O3–SiO2 Glasses Doped with NdF3
Abstract—Sodium borosilicate glasses doped with different content of NdF3 mol % have been prepared by rapid quenching method. Ultrasonic velocities (both longitudinal and shear) measurements have been carried out at room temperature and at ultrasonic frequency of 4 MHz. Elastic moduli, Debye temperature, softening temperature and Poisson's ratio have been obtained as a function of NdF3 modifier...
متن کاملتأثیر عملیات حرارتی و اتمسفر بر خواص مغناطیسی شیشه سرامیک فریت نیکل نانوساختار
The effects of temperature, time and atmosphere on microstructure and magnetic properties of NiFe2O4 glassceramic were investigated utilizing differential thermal analysis, X-ray diffraction, vibrating sample magnetometer and scanning electron microscope techniques. Various compositions were studied in the Na2O-NiO-Fe2O3-B2O3-SiO2 system to obtain amorphous phase. The sample heat-treated in gr...
متن کاملتأثیر عملیات حرارتی و اتمسفر بر خواص مغناطیسی شیشه سرامیک فریت نیکل نانوساختار
در پژوهش حاضر اثر دما، زمان و اتمسفر بر ریزساختار و خواص مغناطیسی فریت نیکل تهیه شده به روش شیشه سرامیک توسط تکنیک های تحلیل حرارتی افتراقی، پراش اشعه x (xrd)، مغناطومتری نمونه مرتعش و میکروسکوپ الکترونی روبشی مورد مطالعه قرار گرفت. ترکیبات مختلف در سیستم sio2- b2o3- fe2o3- nio- na2o برای دست یابی به شیشه آمرف بررسی گردید. نمونه ی عملیات حرارتی شده در بستر گرافیتی در دمای 0c510 به مدت یک ساعت، ...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 34 شماره 2
صفحات 61- 69
تاریخ انتشار 2015-07
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023